Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO/PA C61HL BLACK MITSUBISHI ENGINEERING JAPAN
LEMALLOY™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPO/PA/MITSUBISHI ENGINEERING JAPAN/C61HL BLACK
Melt volume flow rate
280°C/5.0kg
ISO1133
cm3/10min
3
Mechanical performance
Test Condition
Test Method
Unit
PPO/PA/MITSUBISHI ENGINEERING JAPAN/C61HL BLACK
Nominal tensile fracture strain
23°C
ISO527-2
%
4
Tensile modulus
23°C
ISO527-2
Mpa
2
Tensile strain
屈服,23°C
ISO527-2
%
5
Tensile stress
屈服,23°C
ISO527-2
Mpa
6
Bending modulus
23°C
ISO178
Mpa
2
Bending stress
23°C
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PPO/PA/MITSUBISHI ENGINEERING JAPAN/C61HL BLACK
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
9
Electrical performance
Test Condition
Test Method
Unit
PPO/PA/MITSUBISHI ENGINEERING JAPAN/C61HL BLACK
Surface resistivity
IEC60093
ohms
5
Dielectric strength
1.00mm
IEC60243-1
KV/mm
3
Dielectric strength
3.00mm
IEC60243-1
KV/mm
1
Volume resistivity
IEC60093
ohms·cm
1