Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM CH-10 JAPAN POLYPLASTIC
DURACON®
Automotive sector
Carbon fiber reinforced、Conductive、Filler: Carbon fiber rein、10% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
POM/JAPAN POLYPLASTIC/CH-10
Density/specific gravity
ISO1183
g/cm³
1
Melt volume flow rate
190°C/2.16kg
ISO1133
cm3/10min
3
Melt mass flow rate
190°C/2.16kg
ISO1133
g/10min
4
Mechanical performance
Test Condition
Test Method
Unit
POM/JAPAN POLYPLASTIC/CH-10
Tensile modulus
ISO527-2
Mpa
8
Tensile strain
断裂
ISO527-2
%
2
Tensile stress
ISO527-2
Mpa
1
Wear factor
0.49MPa,0.30m/sec4
JISK7218
10^-8mm³/N·m
1
Wear factor
0.060MPa,0.15m/sec5
JISK7218
10^-8mm³/N·m
2
Wear factor
0.49MPa,0.30m/sec6
JISK7218
10^-8mm³/N·m
5
Wear factor
0.060MPa,0.15m/sec7
JISK7218
10^-8mm³/N·m
1
Bending modulus
ISO178
Mpa
7
Bending stress
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
POM/JAPAN POLYPLASTIC/CH-10
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Linear coefficient of thermal expansion
MD：23到55°C
内部方法
cm/cm/°C
2
Linear coefficient of thermal expansion
TD：23to55°C
内部方法
cm/cm/°C
9
Electrical performance
Test Condition
Test Method
Unit
POM/JAPAN POLYPLASTIC/CH-10
Surface resistivity
IEC60093
ohms
5
Volume resistivity
IEC60093
ohms·cm
2
Impact performance
Test Condition
Test Method
Unit
POM/JAPAN POLYPLASTIC/CH-10
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
3