TPV 111-35 CELANESE USA
Santoprene™
Electrical field、Electronic field、Fitness equipment、Automotive sector、Washer、Architectural application、Seals、Application in the automo、Phone、sporting goods、Printing machine parts
Aging resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Thermal performance
Test Condition
Test Method
Unit
TPV/CELANESE USA/111-35
Brittle temperature
ASTMD746
°C
-
Brittle temperature
ISO812
°C
-
ageing
Test Condition
Test Method
Unit
TPV/CELANESE USA/111-35
Changes in tensile stress during fracture
23°C,168hr,inAceticAcid
ISO1817
%
-
Changes in tensile stress during fracture
23°C,168hr,inCyclohexane
ISO1817
%
6
Changes in tensile stress during fracture
23°C,168hr,inDetergent(Tide),2.5%
ISO1817
%
0
Changes in tensile stress during fracture
23°C,168hr,inEthanol,95%
ISO1817
%
3
Changes in tensile stress during fracture
23°C,168hr,inHydrochloricAcid,10%
ISO1817
%
0
Changes in tensile stress during fracture
23°C,168hr,inIsopropylAlcohol
ISO1817
%
5
Changes in tensile stress during fracture
23°C,168hr,inMethylethylketone
ISO1817
%
8
Changes in tensile stress during fracture
23°C,168hr,inSodiumChloride,15%
ISO1817
%
-
Changes in tensile stress during fracture
23°C,168hr,inSodiumHydroxide,50%
ISO1817
%
-
Changes in tensile stress during fracture
23°C,168hr,inSulfuricAcid,98%
ISO1817
%
-
Changes in tensile stress during fracture
23°C,168hr,inTrichloroethylene
ISO1817
%
7
Changes in tensile stress during fracture
100°C,168hr,inDeionizedWater
ISO1817
%
-
Changes in tensile stress during fracture
100°C,168hr,inIRM903Oil
ISO1817
%
-
Changes in tensile stress during fracture
125°C,70hr,inIRM903Oil
ISO1817
%
-
Changes in tensile stress during fracture
125°C,168hr,inIRM903Oil
ISO1817
%
-
Change rate of ultimate elongation
125°C,168hr,inIRM903Oil
ASTMD471
%
-
Change rate of ultimate elongation
23°C,168hr,inAceticAcid
ASTMD471
%
-
Change rate of ultimate elongation
23°C,168hr,inCyclohexane
ASTMD471
%
6
Change rate of ultimate elongation
23°C,168hr,inDetergent(Tide),2.5%
ASTMD471
%
0
Change rate of ultimate elongation
23°C,168hr,inEthanol,95%
ASTMD471
%
3
Change rate of ultimate elongation
23°C,168hr,inHydrochloricAcid,10%
ASTMD471
%
0
Change rate of ultimate elongation
23°C,168hr,inIsopropylAlcohol
ASTMD471
%
5
Change rate of ultimate elongation
23°C,168hr,inMethylethylketone
ASTMD471
%
8
Change rate of ultimate elongation
23°C,168hr,inSodiumChloride,15%
ASTMD471
%
-
Change rate of ultimate elongation
23°C,168hr,inSodiumHydroxide,50%
ASTMD471
%
-
Change rate of ultimate elongation
23°C,168hr,inSulfuricAcid,98%
ASTMD471
%
-
Change rate of ultimate elongation
23°C,168hr,inTrichloroethylene
ASTMD471
%
7
Change rate of ultimate elongation
100°C,168hr,inDeionizedWater
ASTMD471
%
-
Change rate of ultimate elongation
100°C,168hr,inIRM903Oil
ASTMD471
%
-
Change rate of ultimate elongation
125°C,70hr,inIRM903Oil
ASTMD471
%
-
Change rate of ultimate elongation in air
150°C,168hr
ASTMD573
%
-
Change rate of tensile strength in air
150°C,168hr
ASTMD573
%
-
Change rate of tensile strength in air
150°C,168hr
ISO188
%
-
Change rate of tensile strength
23°C,168hr,inAceticAcid
ASTMD471
%
-
Change rate of tensile strength
23°C,168hr,inCyclohexane
ASTMD471
%
4
Change rate of tensile strength
23°C,168hr,inDetergent(Tide),2.5%
ASTMD471
%
-
Change rate of tensile strength
23°C,168hr,inEthanol,95%
ASTMD471
%
-
Change rate of tensile strength
23°C,168hr,inHydrochloricAcid,10%
ASTMD471
%
-
Change rate of tensile strength
23°C,168hr,inIsopropylAlcohol
ASTMD471
%
2
Change rate of tensile strength
23°C,168hr,inMethylethylketone
ASTMD471
%
4
Change rate of tensile strength
23°C,168hr,inSodiumChloride,15%
ASTMD471
%
-
Change rate of tensile strength
23°C,168hr,inSodiumHydroxide,50%
ASTMD471
%
-
Change rate of tensile strength
23°C,168hr,inSulfuricAcid,98%
ASTMD471
%
-
Change rate of tensile strength
23°C,168hr,inTrichloroethylene
ASTMD471
%
5
Change rate of tensile strength
100°C,168hr,inDeionizedWater
ASTMD471
%
-
Change rate of tensile strength
100°C,168hr,inIRM903Oil
ASTMD471
%
-
Change rate of tensile strength
125°C,70hr,inIRM903Oil
ASTMD471
%
-
Change rate of tensile strength
125°C,168hr,inIRM903Oil
ASTMD471
%
-
Change rate of tensile strength
23°C,168hr,inAceticAcid
ISO1817
%
-
Change rate of tensile strength
23°C,168hr,inCyclohexane
ISO1817
%
4
Change rate of tensile strength
23°C,168hr,inDetergent(Tide),2.5%
ISO1817
%
-
Change rate of tensile strength
23°C,168hr,inEthanol,95%
ISO1817
%
-
Change rate of tensile strength
23°C,168hr,inHydrochloricAcid,10%
ISO1817
%
-
Change rate of tensile strength
23°C,168hr,inIsopropylAlcohol
ISO1817
%
2
Change rate of tensile strength
23°C,168hr,inMethylethylketone
ISO1817
%
4
Change rate of tensile strength
23°C,168hr,inSodiumChloride,15%
ISO1817
%
-
Change rate of tensile strength
23°C,168hr,inSodiumHydroxide,50%
ISO1817
%
-
Change rate of tensile strength
23°C,168hr,inSulfuricAcid,98%
ISO1817
%
-
Change rate of tensile strength
23°C,168hr,inTrichloroethylene
ISO1817
%
5
Change rate of tensile strength
100°C,168hr,inDeionizedWater
ISO1817
%
-
Change rate of tensile strength
100°C,168hr,inIRM903Oil
ISO1817
%
-
Change rate of tensile strength
125°C,70hr,inIRM903Oil
ISO1817
%
-
Change rate of tensile strength
125°C,168hr,inIRM903Oil
ISO1817
%
-
Volume change
125°C,70hr,在IRM903油中
ASTMD471
%
1
Volume change
125°C,70hr,在IRM903油中
ISO1817
%
1
Quality change rate
23.0°C,168hr,inTrichloroethylene
ISO1817
%
-
Quality change rate
23.0°C,168hr,inCyclohexane
ISO1817
%
-
Quality change rate
23.0°C,168hr,inSodiumHydroxide,50%
ISO1817
%
-
Quality change rate
23.0°C,168hr,inSodiumChloride,15%
ISO1817
%
0
Quality change rate
23.0°C,168hr,inHydrochloricAcid,10%
ISO1817
%
0
Quality change rate
23.0°C,168hr,inEthanol,95%
ISO1817
%
0
Quality change rate
23.0°C,168hr,inDetergent(Tide),2.5%
ISO1817
%
0
Quality change rate
100°C,168hr,inDeionizedWater
ISO1817
%
6
Quality change rate
23.0°C,168hr,inAceticAcid
ISO1817
%
6
Quality change rate
23.0°C,168hr,inSulfuricAcid,98%
ISO1817
%
7
Quality change rate
23°C,168hr,inMethylethylketone
ASTMD471
%
-
Quality change rate
23°C,168hr,inSodiumChloride,15%
ASTMD471
%
0
Quality change rate
23°C,168hr,inSodiumHydroxide,50%
ASTMD471
%
-
Quality change rate
23°C,168hr,inSulfuricAcid,98%
ASTMD471
%
7
Quality change rate
23°C,168hr,inTrichloroethylene
ASTMD471
%
-
Quality change rate
100°C,168hr,inDeionizedWater
ASTMD471
%
6
Quality change rate
100°C,168hr,inIRM903Oil
ASTMD471
%
9
Quality change rate
125°C,168hr,inIRM903Oil
ASTMD471
%
1
Quality change rate
23.0°C,168hr,inMethylethylketone
ISO1817
%
-
Quality change rate
23.0°C,168hr,inIsopropylAlcohol
ISO1817
%
-
Quality change rate
23°C,168hr,inAceticAcid
ASTMD471
%
6
Quality change rate
23°C,168hr,inCyclohexane
ASTMD471
%
-
Quality change rate
23°C,168hr,inDetergent(Tide),2.5%
ASTMD471
%
0
Quality change rate
23°C,168hr,inEthanol,95%
ASTMD471
%
0
Quality change rate
23°C,168hr,inHydrochloricAcid,10%
ASTMD471
%
0
Quality change rate
23°C,168hr,inIsopropylAlcohol
ASTMD471
%
-
Quality change rate
100°C,168hr,inIRM903Oil
ISO1817
%
9
Quality change rate
125°C,168hr,inIRM903Oil
ISO1817
%
1
elastomer
Test Condition
Test Method
Unit
TPV/CELANESE USA/111-35
CompressionSet4
23°C,22hr
ASTMD395B
%
1
CompressionSet4
125°C,70hr
ASTMD395B
%
3
TearStrength-AcrossFlow3
23°C
ISO34-1
kN/m
1
Tensile strength - transverse flow rate
断裂,23°C
ASTMD412
Mpa
2
Tensile strength TD
Break,23°C
ISO37
Mpa
2
Tensile stress transverse flow rate
100%应变,23°C
ASTMD412
Mpa
1
Tensile stress transverse flow rate
100%应变,23°C
ISO37
Mpa
1
Elongation rate - lateral flow rate
断裂,23°C
ASTMD412
%
3
Elongation rate - lateral flow rate
断裂,23°C
ISO37
%
3
Tear strength - transverse flow rate 2
23°C
ASTMD624
kN/m
1
Compression permanent deformation 4
23°C,22hr
ISO815
%
1
Compression permanent deformation 4
125°C,70hr
ISO815
%
3