Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 1013NW8 UBE JAPAN
UBE
--
Low viscosity、Fast forming cycle
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PA6/UBE JAPAN/1013NW8
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
1
Mechanical performance
Test Condition
Test Method
Unit
PA6/UBE JAPAN/1013NW8
elongation at break
ASTM D638/ISO 527
%
6
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
8
elongation
ASTM D638/ISO 527
%
8
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
4
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
6
Tensile elongation at break (elongation at break)
ASTM D638/ISO 527
%
1
Thermal performance
Test Condition
Test Method
Unit
PA6/UBE JAPAN/1013NW8
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
7
Linear expansion coefficient
ASTM D696/ISO 11359
mm/mm.℃
8
Electrical performance
Test Condition
Test Method
Unit
PA6/UBE JAPAN/1013NW8
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
1