Density/specific gravity

ISO1183

g/cm³

1

Melt mass flow rate

190°C/2.16kg

ISO1133

g/10min

2

Shrinkage rate

TD

ISO294-4

%

1

Shrinkage rate

MD

ISO294-4

%

1

Water absorption rate

平衡,23°C,2.00mm,50%RH

ISO62

%

0

Nominal tensile fracture strain

ISO527-2

%

1

Tensile modulus

ISO527-2

Mpa

3

Tensile strain

屈服

ISO527-2

%

1

Tensile stress

屈服

ISO527-2

Mpa

7

Bending modulus

ISO178

Mpa

3

Hot deformation temperature

0.45MPa,未退火

ISO75-2/B

°C

1

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

9

Melting temperature 2

ISO11357-3

°C

1

Linear coefficient of thermal expansion

MD：23到55°C

ASTME831

cm/cm/°C

9

Linear coefficient of thermal expansion

MD

ISO11359-2

cm/cm/°C

1

Linear coefficient of thermal expansion

TD：--

ISO11359-2

cm/cm/°C

1

Linear coefficient of thermal expansion

TD：-40to23°C

ISO11359-2

cm/cm/°C

9

Linear coefficient of thermal expansion

TD：AnnealingTemperature

ISO11359-2

°C

1

Linear coefficient of thermal expansion

TD：AnnealingTime-Optional

ISO11359-2

min/mm

3

Charpy Notched Impact Strength

-30°C

ISO179/1eA

kJ/m²

6

Charpy Notched Impact Strength

23°C

ISO179/1eA

kJ/m²

7

Impact strength of simply supported beam without notch

23°C

ISO179/1eU

kJ/m²

1

Impact strength of cantilever beam gap

-40°C

ISO180/1A

kJ/m²

7

Impact strength of cantilever beam gap

23°C

ISO180/1A

kJ/m²

7

Extreme Oxygen Index

ISO4589-2

%

2

Burning rate 3

1.00mm

ISO3795

mm/min

2

atomization

F-value(refraction)

ISO6452

%

9

atomization

G-value(condensate)

ISO6452

g

2

Emission

VDA275

mg/kg

<

EmissionofOrganicCompounds

VDA277

µgC/g

4