Melt volume flow rate

280°C/5.0kg

ISO1133

cm3/10min

1

Melt mass flow rate

280°C/5.0kg

ASTMD1238

g/10min

1

Shrinkage rate

MD：3.20mm

内部方法

%

0

Water absorption rate

饱和,23°C

ISO62

%

0

Tensile strength 3

屈服

ASTMD638

Mpa

7

Tensile strength 3

断裂

ASTMD638

Mpa

5

Tensile modulus

ISO527-2/1

Mpa

2

Tensile modulus 2

ASTMD638

Mpa

2

Tensile strain

屈服

ISO527-2/50

%

3

Tensile strain

断裂

ISO527-2/50

%

7

Tensile stress

断裂

ISO527-2/50

Mpa

5

Tensile stress

屈服

ISO527-2/50

Mpa

7

Elongation rate 3

屈服

ASTMD638

%

4

Elongation rate 4

断裂

ASTMD638

%

8

Bending modulus 4

50.0mm跨距

ASTMD790

Mpa

3

Bending modulus 5

ISO178

Mpa

2

Bending strength 4

屈服,50.0mm跨距

ASTMD790

Mpa

1

Bending strength 5,6

ISO178

Mpa

1

Hot deformation temperature

1.8MPa,未退火,3.20mm

ASTMD648

°C

1

Hot deformation temperature 9

1.8MPa,Unannealed,64.0mmSpan

ISO75-2/Af

°C

1

Vicat softening temperature

ASTMD152510

°C

1

Vicat softening temperature

--

ISO306/B50

°C

1

Vicat softening temperature

--

ISO306/B120

°C

1

Linear coefficient of thermal expansion

MD：-40到40°C

ASTME831

cm/cm/°C

5

Linear coefficient of thermal expansion

MD：-40到40°C

ISO11359-2

cm/cm/°C

5

Linear coefficient of thermal expansion

TD：-40到40°C

ASTME831

cm/cm/°C

5

Linear coefficient of thermal expansion

TD：-40到40°C

ISO11359-2

cm/cm/°C

5

Impact strength of simply supported beam gap 7

23°C

ISO179/1eA

kJ/m²

6

Suspended wall beam gap impact strength 8

-30°C

ISO180/1A

kJ/m²

4

Suspended wall beam gap impact strength 8

23°C

ISO180/1A

kJ/m²

6

Dart impact equipped with measuring instruments

23°C,TotalEnergy

ASTMD3763

J

4