Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM/PTFE KL004A WHNAT SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electrical appliances、Electronic and Electrical、Plastic bag、Industrial applications
wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/KL004A WHNAT |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 95.0 °C |
| 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 98.0 °C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/KL004A WHNAT |
|---|---|---|---|
| Tensile Elongation | 断裂 | ASTMD638 | 11 % |
| Flexural Modulus | ASTMD790 | 2620 Mpa | |
| Flexural Strength | 86.0 Mpa | ||
| Coefficient of Friction | Dynamic | ASTMD3702Modified | 0.23 |
| Tensile Modulus | ISO527-2/1 | 2700 Mpa | |
| Flexural Modulus | ISO178 | 2900 Mpa | |
| Coefficient of Friction | Static | ASTMD3702Modified | 0.091 |
| Specific Wear Rate | 12.0 10^-10in^5-min/ft-lb-hr | ||
| Tensile Strain | 断裂 | ISO527-2 | 9.4 % |
| Tensile Stress | 50.6 Mpa | ||
| Flexural Stress | ISO178 | 86.5 Mpa | |
| Tensile Modulus | ASTMD638 | 2550 Mpa | |
| Tensile Strength | 断裂 | 56.1 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/KL004A WHNAT |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.37 % |
| 24hr,50%RH | ASTMD570 | 0.23 % | |
| Modeling Shrinkage | MD：24小时 | ASTMD955 | 2.0to2.2 % |
| TD：24hr | 2.0to2.2 % | ||
| TD:24小时 | ISO294-4 | 2.0to2.2 % | |
| MD:24小时 | 2.0to2.2 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/KL004A WHNAT |
|---|---|---|---|
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 7.20 J |
| 23°C | ISO180/1U | 39 kJ/m² | |
| Notched Izod Impact Strength | ISO180/1A | 4.5 kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO6603-2 | 0.960 J |