PC/ABS C1200 GY6977 SABIC INNOVATIVE SINGAPHORE
CYCOLOY™
Electrical field、Electronic field、Automotive interior parts
High impact resistance、heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE SINGAPHORE/C1200 GY6977
Melt Volume-Flow Rate (MVR)
265°C/5.0kg
ISO1133
cm3/10min
2
Melt mass flow rate
260°C/5.0kg
ASTMD1238
g/10min
1
Shrinkage rate
MD：3.20mm
内部方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE SINGAPHORE/C1200 GY6977
Tensile modulus
ASTMD638
Mpa
2
Tensile modulus
ISO527-2/1
Mpa
2
tensile strength
屈服
ASTMD638
Mpa
5
tensile strength
屈服
ISO527-2/50
Mpa
5
elongation
屈服
ASTMD638
%
5
elongation
屈服
ISO527-2/50
%
4
elongation
断裂
ASTMD638
%
1
elongation
断裂
ISO527-2/50
%
1
Bending modulus
50.0mm跨距
ASTMD790
Mpa
2
Bending modulus
ISO178
Mpa
2
bending strength
ISO178
Mpa
8
bending strength
屈服,50.0mm跨距
ASTMD790
Mpa
8
Suspended wall beam gap impact strength
-30°C
ISO180/1A
kJ/m²
3
Suspended wall beam gap impact strength
23°C
ISO180/1A
kJ/m²
4
Dart impact equipped with measuring instruments
-30°C,TotalEnergy
ASTMD3763
J
5
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
5
Thermal performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE SINGAPHORE/C1200 GY6977
RTI Imp
UL746
°C
8
RTIElec
UL746
°C
1
RTIStr
UL746
°C
1
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
0.45MPa,Unannealed,64.0mmSpan
ISO75-2/Bf
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,64.0mm跨距
ISO75-2/Af
°C
1
vicat softening point
ISO306/B50
°C
1
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
7