Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC CF-3200HW K25351 LOTTE KOREA
INFINO®
Phone
Glass fiber reinforced、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/LOTTE KOREA/CF-3200HW K25351
Density/specific gravity
本色
ASTM D792, ISO 1183
g/cm³
1
Melt flow rate
250°C/10.0 kg
ASTM D1238, ISO 1133
g/10 min
2
Shrinkage rate
流动 : 3.20 mm
ASTM D955
%
0
Shrinkage rate
横向流动 : 3.20 mm
ASTM D955
%
0
Shrinkage rate
横向流量 : 2.00 mm
ISO 294-4
%
0
Shrinkage rate
流量 : 2.00 mm
ISO 294-4
%
0
Water absorption rate
饱和, 23°C
ASTM D570, ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/LOTTE KOREA/CF-3200HW K25351
Tensile strength
屈服 3
ASTM D638
Mpa
9
Tensile strength
屈服
ISO 527-2/5
Mpa
1
Tensile strength
断裂 3
ASTM D638
Mpa
9
Tensile strength
断裂
ISO 527-2/5
Mpa
2
Tensile modulus
-- 3
ASTM D638
Mpa
5
Tensile modulus
--
ISO 527-2/5
Mpa
5
elongation
断裂 3
ASTM D638
%
4
elongation
断裂
ISO 527-2/5
%
4
Bending modulus
-- 4
ASTM D790
Mpa
5
Bending modulus
-- 5
ISO 178
Mpa
6
bending strength
-- 4
ASTM D790
Mpa
1
bending strength
-- 5
ISO 178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PC/LOTTE KOREA/CF-3200HW K25351
Vicat softening temperature
ISO 306/B50
°C
1
Thermal deformation temperature under load
0.45 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Thermal deformation temperature under load
0.45 MPa, 未退火, 4.00 mm
ISO 75-2/B
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm
ISO 75-2/A
°C
1
Impact performance
Test Condition
Test Method
Unit
PC/LOTTE KOREA/CF-3200HW K25351
Charpy Notched Impact Strength
23°C
ISO 179/1eA
kJ/m²
2
Impact strength of cantilever beam gap
23°C, 3.18 mm
ASTM D256
J/m
1
Impact strength of cantilever beam gap
23°C, 6.35 mm
ASTM D256
J/m
2
Impact strength of cantilever beam gap
23°C 6
ISO 180/1A
kJ/m²
1