Certificates
PBT B4406G3 Q117 BASF GERMANY
Ultradur®
Thin walled components、Electrical components、switch、Connector、Shell
High mobility、Flame retardant、Glass fiber reinforced、Filler: Glass fiber reinf、30% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/BASF GERMANY/B4406G3 Q117
Density/specific gravity
ISO1183
g/cm³
1
Melt volume flow rate
250°C/2.16kg
ISO1133
cm3/10min
1
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Viscosity value
降低的粘度
ISO1628
ml/g
1
Mechanical performance
Test Condition
Test Method
Unit
PBT/BASF GERMANY/B4406G3 Q117
Tensile modulus
23°C
ISO527-2
Mpa
6
Tensile strain
断裂,23°C
ISO527-2
%
2
Tensile stress
断裂,23°C
ISO527-2
Mpa
1
Bending modulus
23°C
ISO178
Mpa
6
Thermal performance
Test Condition
Test Method
Unit
PBT/BASF GERMANY/B4406G3 Q117
RTIElec
3.0mm
UL746
°C
1
RTIElec
0.40mm
UL746
°C
7
RTIElec
0.75mm
UL746
°C
1
RTIElec
1.5mm
UL746
°C
1
Evolution Calendar intelligent importer
0.40mm
UL746
°C
7
Evolution Calendar intelligent importer
0.75mm
UL746
°C
1
Evolution Calendar intelligent importer
1.5mm
UL746
°C
1
Evolution Calendar intelligent importer
3.0mm
UL746
°C
1
RTIStr
0.40mm
UL746
°C
7
RTIStr
0.75mm
UL746
°C
1
RTIStr
1.5mm
UL746
°C
1
RTIStr
3.0mm
UL746
°C
1
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Melting temperature (DSC)
ISO3146
°C
2
Electrical performance
Test Condition
Test Method
Unit
PBT/BASF GERMANY/B4406G3 Q117
Volume resistivity
IEC60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PBT/BASF GERMANY/B4406G3 Q117
Charpy Notched Impact Strength
23°C
ISO179
kJ/m²
6
Charpy Notched Impact Strength
-30°C
ISO179
kJ/m²
6
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
3
Impact strength of cantilever beam gap
-30°C
ISO180
kJ/m²
6
Impact strength of cantilever beam gap
23°C
ISO180
kJ/m²
6