Shrinkage rate

流动 : 24小时

ASTM D955

%

0

Shrinkage rate

横向流动 : 24小时

ASTM D955

%

0

Water absorption rate

24 hr, 50% RH

ASTM D570

%

1

Tensile strength

屈服 3

ASTM D638

Mpa

3

Tensile strength

屈服

ISO 527-2/5

Mpa

3

Tensile strength

断裂 3

ASTM D638

Mpa

3

Tensile strength

断裂

ISO 527-2/5

Mpa

3

Tensile modulus

-- 2

ASTM D638

Mpa

2

Tensile modulus

--

ISO 527-2/1

Mpa

2

elongation

屈服 3

ASTM D638

%

3

elongation

屈服

ISO 527-2/5

%

3

elongation

断裂 3

ASTM D638

%

6

elongation

断裂

ISO 527-2/5

%

2

Bending modulus

50.0 mm 跨距 4

ASTM D790

Mpa

2

Bending modulus

-- 5

ISO 178

Mpa

1

Bending stress

-- 5, 6

ISO 178

Mpa

5

Bending stress

断裂, 50.0 mm 跨距 4

ASTM D790

Mpa

6

Linear coefficient of thermal expansion

流动 : -40 到 40°C

ASTM E831

cm/cm/°C

9

Linear coefficient of thermal expansion

流动 : 23 到 60°C

ISO 11359-2

cm/cm/°C

9

Linear coefficient of thermal expansion

横向 : -40 到 40°C

ASTM E831

cm/cm/°C

1

Linear coefficient of thermal expansion

横向 : 23 到 60°C

ISO 11359-2

cm/cm/°C

1

Thermal deformation temperature under load

0.45 MPa, 未退火, 3.20 mm

ASTM D648

°C

8

Thermal deformation temperature under load

0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7

ISO 75-2/Bf

°C

9

Thermal deformation temperature under load

1.8 MPa, 未退火, 3.20 mm

ASTM D648

°C

7

Thermal deformation temperature under load

1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7

ISO 75-2/Af

°C

7

Surface resistivity

ASTM D257

ohms

1

Dart impact equipped with measuring instruments

23°C, Energy at Peak

ASTM D3763

J

3