Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 R530HR BK652 ASCEND USA
Vydyne®
Automotive components
Chemical resistance、Fatigue resistance、High mobility、Solvent resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/ASCEND USA/R530HR BK652
Shrinkage rate
TD:23°C,2.00mm
ISO294-4
%
0
Shrinkage rate
MD:23°C,2.00mm
ISO294-4
%
0
Water absorption rate
23°C,24hr
ISO62
%
0
Water absorption rate
平衡,50%RH
ISO62
%
1
Mechanical performance
Test Condition
Test Method
Unit
PA66/ASCEND USA/R530HR BK652
Tensile modulus
23°C
ISO527-2
Mpa
9
Tensile strain
断裂,23°C
ISO527-2
%
4
Tensile stress
断裂,23°C
ISO527-2
Mpa
1
Bending modulus
23°C
ISO178
Mpa
9
Bending stress
23°C
ISO178
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PA66/ASCEND USA/R530HR BK652
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Melting temperature
ISO11357-3
°C
2
Linear coefficient of thermal expansion
MD：23to55°C,2.00mm
ISO11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
TD：23to55°C,2.00mm
ISO11359-2
cm/cm/°C
1
Impact performance
Test Condition
Test Method
Unit
PA66/ASCEND USA/R530HR BK652
Impact strength of simply supported beam without notch
-30°C
ISO179
kJ/m²
8
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
9