Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC BPL1000-701 SABIC INNOVATIVE NANSHA
LEXAN™
Thin walled products、Electronic and electrical、Automotive components
UV resistance、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/BPL1000-701
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
2
Melt mass flow rate
300°C/1.2kg
ASTMD1238
g/10min
2
Shrinkage rate
MD：--2
内部方法
%
0
Shrinkage rate
MD：3.20mm
内部方法
%
0
Shrinkage rate
TD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/BPL1000-701
FlexuralStrength5
Yield,50.0mmSpan
ASTMD790
Mpa
1
Tensile strength 4
屈服
ASTMD638
Mpa
6
Tensile modulus
ISO527-2/1
Mpa
2
Tensile modulus 3
ASTMD638
Mpa
2
Tensile strength 4
Break
ASTMD638
Mpa
5
Tensile strain
断裂
ISO527-2/50
%
9
Tensile strain
屈服
ISO527-2/50
%
4
Tensile stress
断裂
ISO527-2/50
Mpa
5
Tensile stress
屈服
ISO527-2/50
Mpa
6
Elongation rate 4
屈服
ASTMD638
%
4
Elongation rate 4
断裂
ASTMD638
%
9
Bending modulus 5
50.0mmSpan
ASTMD790
Mpa
2
Bending modulus 6
ISO178
Mpa
2
Bending strength 6,7
ISO178
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/BPL1000-701
RTIElec
UL746
°C
8
Evolution Calendar intelligent importer
UL746
°C
8
RTIStr
UL746
°C
8
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature 10
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
9
Vicat softening temperature
ASTMD152511
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
MD：-40到40°C
ISO11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：-40到40°C
ISO11359-2
cm/cm/°C
7
Electrical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/BPL1000-701
Surface resistivity
IEC60093
ohms
>
Dielectric strength
1.60mm,inOil
ASTMD149
KV/mm
2
Leakage Trace Index
IEC60112
V
2
Volume resistivity
IEC60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/BPL1000-701
CharpyNotchedImpact Strength8
23°C
ISO179/1eA
kJ/m²
1
Suspended wall beam gap impact strength 9
-30°C
ISO180/1A
kJ/m²
1
Suspended wall beam gap impact strength 9
23°C
ISO180/1A
kJ/m²
1
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
4
flammability
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/BPL1000-701
Extreme Oxygen Index
ISO4589-2
%
3
Hot filament ignition temperature
1.0mm
IEC60695-2-13
°C
8
Burning wire flammability index
1.0mm
IEC60695-2-12
°C
9