Melt volume flow rate

280°C/5.0kg

ISO1133

cm3/10min

1

Melt mass flow rate

280°C/5.0kg

ASTMD1238

g/10min

1

Shrinkage rate

MD2

内部方法

%

1

Shrinkage rate

MD:3.20mm

内部方法

%

1

Shrinkage rate

TD:3.20mm

内部方法

%

1

Water absorption rate

饱和,23°C

ISO62

%

3

Water absorption rate

平衡,23°C,50%RH

ISO62

%

1

Tensile strength

屈服4

ASTMD638

Mpa

6

Tensile strength

屈服

ISO527-2/50

Mpa

6

Tensile strength

断裂4

ASTMD638

Mpa

5

Tensile strength

断裂

ISO527-2/50

Mpa

5

Tensile modulus

--3

ASTMD638

Mpa

2

Tensile modulus

--

ISO527-2/1

Mpa

2

elongation

屈服4

ASTMD638

%

5

elongation

屈服

ISO527-2/50

%

4

elongation

断裂4

ASTMD638

%

6

elongation

断裂

ISO527-2/50

%

2

Bending modulus

50.0mm跨距5

ASTMD790

Mpa

2

Bending modulus

--6

ISO178

Mpa

2

Bending stress

--6,7

ISO178

Mpa

9

Bending stress

屈服,50.0mm跨距5

ASTMD790

Mpa

9

thermal conductivity

ISO8302

W/m/K

0

Hot deformation temperature

0.45MPa,未退火,3.20mm

ASTMD648

°C

1

Hot deformation temperature

0.45MPa,未退火,100mm跨距10

ISO75-2/Be

°C

1

Vicat softening temperature

--

ASTM D-596

°C

2

Vicat softening temperature

--

ISO306/A50

°C

2

Vicat softening temperature

--

ISO306/B50

°C

2

Linear coefficient of thermal expansion

MD:-40到40°C

ASTME831

cm/cm/°C

7

Linear coefficient of thermal expansion

MD:23到60°C

ISO11359-2

cm/cm/°C

8

Linear coefficient of thermal expansion

TD:-40到40°C

ASTME831

cm/cm/°C

8

Linear coefficient of thermal expansion

TD:23到60°C

ISO11359-2

cm/cm/°C

7

Impact strength of simply supported beam gap 8

-30°C

ISO179/1eA

kJ/m²

1

Impact strength of simply supported beam gap 8

23°C

ISO179/1eA

kJ/m²

2

Dart impact equipped with measuring instruments

23°C,TotalEnergy

ASTMD3763

J

6

Ball pressure hardness

H358/30

ISO2039-1

Mpa

8