Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS 6165A6 SF3001 CELANESE USA
FORTRON®
Pump parts、Electrical/Electronic App、Shell、Fiber grade
Glass fiber reinforced、Flame retardant、standard、High temperature resistan、Filler: Glass mineral、65% filler by weight、65% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPS/CELANESE USA/6165A6 SF3001
SpecificHeatCapacity of Melt
内部方法
J/kg/°C
1
Density/specific gravity
ISO 1183
g/cm³
1
Density/specific gravity
ISO1183
g/cm³
1
Density/specific gravity
ASTMD792
g/cm³
2
Mold shrinkage rate
ISO 2577
%
0
Shrinkage rate
MD
ASTMD955
%
0
Shrinkage rate
TD
ASTMD955
%
0
Shrinkage rate
TD
ISO294-4
%
0
Shrinkage rate
MD
ISO294-4
%
0
Specific volume
ASTMD792
cm³/g
0
Water absorption rate
饱和,23°C
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPS/CELANESE USA/6165A6 SF3001
IZOD notch impact strength
23℃
ISO 180/1A
kJ/m²
6
Tensile strength
断裂,23°C
ASTMD638
Mpa
1
Tensile modulus
ISO527-2/1A/1
Mpa
1
Tensile modulus
ISO 527-1
Mpa
1
tensile strength
ISO 527-1
Mpa
1
Tensile strain
断裂
ISO527-2/1A/5
%
1
Tensile stress
断裂
ISO527-2/1A/5
Mpa
1
Rockwell hardness
ISO 2039-2
M-scale
1
elongation
断裂
ISO 527-1
%
1
elongation
断裂,23°C
ASTMD638
%
1
Bending modulus
ISO 178
Mpa
1
Bending modulus
23°C
ISO178
Mpa
1
bending strength
ISO 178
Mpa
2
Bending stress 2
ISO178
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PPS/CELANESE USA/6165A6 SF3001
Glass transition temperature 3
ISO11357-2
°C
9
Hot deformation temperature
0.45MPa,退火
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Hot deformation temperature
8.0MPa,未退火
ISO75-2/C
°C
2
Hot deformation temperature
1.80Mpa
ISO 75-1
°C
2
Melting temperature 5
ISO11357-3
°C
2
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD
ISO11359-2
cm/cm/°C
2
Electrical performance
Test Condition
Test Method
Unit
PPS/CELANESE USA/6165A6 SF3001
Surface resistivity
IEC60093
ohms
>
Dielectric strength
IEC60243-1
KV/mm
2
Leakage Trace Index
IEC60112
V
1
Arc resistance
ASTMD495
sec
1
Volume resistivity
ASTMD257
ohms·cm
1
Volume resistivity
IEC60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PPS/CELANESE USA/6165A6 SF3001
Charpy Notched Impact Strength
-30°C
ISO179/1eA
kJ/m²
7
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
7
Impact strength of simply supported beam without notch
-30°C
ISO179/1eU
kJ/m²
2
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
2
Unscented Izod impact strength
23°C
ISO180/1U
kJ/m²
2
Impact strength of cantilever beam gap
-30°C
ISO180/1A
kJ/m²
6
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
6
Basic performance
Test Condition
Test Method
Unit
PPS/CELANESE USA/6165A6 SF3001
Water absorption rate
23℃
ISO 62
%
0