density

ASTMD792

g/cm³

1

Melt viscosity

240°C,1000sec^-1

ASTMD3835

Pa·s

2

Melt mass flow rate

230°C/3.8kg

ASTMD1238

g/10min

1

Melt mass flow rate

220°C/10.0kg

ISO1133

g/10min

8

Shrinkage rate

MD：3.20mm

内部方法

%

0

Tensile strength

屈服

ASTMD638

Mpa

3

Tensile strength

断裂

ASTMD638

Mpa

3

Tensile modulus

ASTMD638

Mpa

2

Tensile modulus

ISO527-2/1

Mpa

2

Tensile strain

断裂

ISO527-2/50

%

2

Tensile strain

屈服

ISO527-2/50

%

2

Tensile stress

屈服

ISO527-2/50

Mpa

4

Tensile stress

断裂

ISO527-2/50

Mpa

3

elongation

断裂

ASTMD638

%

2

elongation

屈服

ASTMD638

%

2

Bending modulus

50.0mm跨距

ASTMD790

Mpa

2

Bending modulus

ISO178

Mpa

1

bending strength

ISO178

Mpa

6

bending strength

屈服,50.0mm跨距

ASTMD790

Mpa

6

RTIElec

UL746

°C

6

Evolution Calendar intelligent importer

UL746

°C

6

RTIStr

UL746

°C

6

Hot deformation temperature

0.45MPa,未退火,3.20mm

ASTMD648

°C

9

Hot deformation temperature

1.8MPa,未退火,3.20mm

ASTMD648

°C

7

Hot deformation temperature

1.8MPa,Unannealed,64.0mmSpan

ISO75-2/Af

°C

7

Vicat softening temperature

ASTMD15259

°C

9

Vicat softening temperature

ISO306/B50

°C

9

Linear coefficient of thermal expansion

MD：-40到40°C

ASTME831

cm/cm/°C

9

Linear coefficient of thermal expansion

TD：-40到40°C

ASTME831

cm/cm/°C

9

Impact strength of cantilever beam gap

23°C

ASTMD256

J/m

4

Impact strength of cantilever beam gap

-30°C

ISO180/1A

kJ/m²

1

Impact strength of cantilever beam gap

23°C

ISO180/1A

kJ/m²

3

Dart impact equipped with measuring instruments

23°C,TotalEnergy

ASTMD3763

J

2