Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC ML6411 7T1D043L SABIC INNOVATIVE NANSHA
LEXAN™
Electrical appliances、Electronic display、Architectural Application、Lighting applications
Easy to form、Short molding cycle、Low temperature and high
MSDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/ML6411 7T1D043L
Melt flow rate
260°C/2.16 kg
ASTM D1238
g/10 min
7
Molten Volume Flow Rate (MVR)
260°C/5.0 kg
ISO 1133
cm3/10min
1
Shrinkage rate - flow
3.20 mm
内部方法
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/ML6411 7T1D043L
Tensile strength
屈服 3
ASTM D638
Mpa
6
Tensile strength
屈服
ISO 527-2/50
Mpa
6
Tensile strength
断裂 3
ASTM D638
Mpa
5
Tensile strength
断裂
ISO 527-2/50
Mpa
5
Tensile modulus
-- 2
ASTM D638
Mpa
2
Tensile modulus
--
ISO 527-2/1
Mpa
2
elongation
屈服 3
ASTM D638
%
5
elongation
屈服
ISO 527-2/50
%
5
elongation
断裂 3
ASTM D638
%
1
elongation
断裂
ISO 527-2/50
%
1
Bending modulus
50.0 mm 跨距 4
ASTM D790
Mpa
2
Bending modulus
-- 5
ISO 178
Mpa
2
Bending stress
-- 5, 6
ISO 178
Mpa
9
Bending stress
屈服, 50.0 mm 跨距 4
ASTM D790
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/ML6411 7T1D043L
RTI
UL 746
°C
1
RTI Elec
UL 746
°C
1
RTI Imp
UL 746
°C
1
Vicat softening temperature
--
ASTM D15259, ISO 306/B509
°C
1
Vicat softening temperature
--
ISO 306/B120
°C
1
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ASTM E831
cm/cm/°C
7
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ISO 11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
横向 : -40 到 40°C
ASTM E831
cm/cm/°C
5
Linear coefficient of thermal expansion
横向 : -40°C
ISO 11359-2
cm/cm/°C
7
Thermal deformation temperature under load
0.45 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Thermal deformation temperature under load
0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 8
ISO 75-2/Be
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 8
ISO 75-2/Ae
°C
1
Electrical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/ML6411 7T1D043L
Dielectric strength
3.20 mm, in Oil
ASTM D149
KV/mm
2
Leakage Trace Index
IEC 60112
V
2
Volume resistivity
IEC 60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/ML6411 7T1D043L
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
7
flammability
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/ML6411 7T1D043L
Hot filament ignition temperature
1.0 mm
IEC 60695-2-13
°C
8
Hot filament ignition temperature
2.0 mm
IEC 60695-2-13
°C
8
Hot filament ignition temperature
3.0 mm
IEC 60695-2-13
°C
8
Burning wire flammability index
1.0 mm
IEC 60695-2-12
°C
9