Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS PA-777D TAIWAN CHIMEI
POLYLAC®
Electrical field、Electronic field、Home appliance components、Automotive sector
heat-resisting、Medium impact resistance
MSDS
RoHS
UL
SGS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-777D
Density/specific gravity
--3
ASTMD792
g/cm³
1
Density/specific gravity
23°C
ISO1183
g/cm³
1
Melt volume flow rate
220°C/10.0kg
ISO1133
cm3/10min
5
Melt mass flow rate
220°C/10.0kg
ASTMD1238
g/10min
5
Shrinkage rate
ISO294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-777D
Tensile strength
屈服4
ASTMD638
Mpa
4
Tensile strength
屈服
ISO527-2/50
Mpa
4
Tensile strength
断裂
ISO527-2/50
Mpa
3
elongation
断裂4
ASTMD638
%
1
elongation
断裂
ISO527-2/50
%
3
Bending modulus
--5
ASTMD790
Mpa
2
Bending modulus
--6
ISO178
Mpa
2
bending strength
--5
ASTMD790
Mpa
6
bending strength
--6
ISO178
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-777D
Hot deformation temperature
1.8MPa,未退火
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
9
Hot deformation temperature
1.8MPa,退火
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,退火
ISO75-2/A
°C
1
Vicat softening temperature
--
ASTMD15257
°C
1
Vicat softening temperature
--
ISO306/A50
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
8
Impact performance
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-777D
Charpy Notched Impact Strength
-30°C
ISO179
kJ/m²
7
Charpy Notched Impact Strength
23°C
ISO179
kJ/m²
1
Impact strength of cantilever beam gap
23°C,3.20mm
ASTMD256
J/m
1
Impact strength of cantilever beam gap
23°C,6.40mm
ASTMD256
J/m
1
Impact strength of cantilever beam gap
-30°C
ISO180/1A
kJ/m²
7
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
1