Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 1101G-X50 TORAY JAPAN
Toraycon®
Electrical field、Electronic field、Automotive sector
Glass fiber reinforced、Flame retardant、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1101G-X50
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
0
physical property
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1101G-X50
Shrinkage rate
MD
ISO294-4
%
0
Shrinkage rate
TD
ISO294-4
%
0
Water absorption rate
(23°C,24hr)
ISO62
%
0
Water absorption rate
23℃,24hr
ASTM D570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1101G-X50
IZOD notch impact strength
缺口，23℃
ASTM D256
J/m
7
IZOD notch impact strength
缺口，-40℃
ASTM D256
J/m
6
IZOD notch impact strength
无缺口，23℃
ASTM D256
KJ/m
4
IZOD notch impact strength
无缺口，-40℃
ASTM D256
KJ/m
2
elongation at break
23°C
ISO527-2
%
2
elongation at break
ASTM D638/ISO 527
%
4
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
8
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
4
Tensile modulus
23°C
ISO527-2
Mpa
1
tensile strength
23℃
ASTM D638
Mpa
1
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
1
tensile strength
23°C
ISO527-2
Mpa
1
Rockwell hardness
ASTM D785
M
9
elongation
23℃
ASTM D638
%
4
Bending modulus
23°C
ISO178
Mpa
9
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
8
Bending modulus
23℃
ASTM D790
GPa
8
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
bending strength
23°C
ISO178
Mpa
2
bending strength
23℃
ASTM D790
Mpa
2
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
7
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
6
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
4
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
2
Thermal performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1101G-X50
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
2
Hot deformation temperature
0.45MPa未退火
ISO75-2/Bf
°C
2
Hot deformation temperature
1.80MPa退火
ISO75-2/Af
°C
2
Hot deformation temperature
-，0.45MPa
ASTM D648
°C
2
Hot deformation temperature
-，1.82Mpa
ASTM D648
°C
2
Coefficient of linear expansion
MD
ISO11359-2
cm/cm/°C
4
Linear expansion coefficient
ASTM D696/ISO 11359
mm/mm.℃
2
Electrical performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1101G-X50
Dissipation factor
23°C
IEC60250
1MHz
0
Dissipation factor
耐电弧性
IEC61621
S
1
Dielectric constant
23°C
IEC60250
1MHz
3
Insulation strength
IEC60243-1
KV/mm
2
Voltage endurance
ASTM D149
MV/m
2
Volume resistance
IEC60093
Ω.cm
4
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
2
Volume resistivity
ASTM D495
S
1
hardness
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1101G-X50
Rockwell hardness
ISO2039-2
M（Scale）
9