Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS A673M B TORAY SHENZHEN
Torelina®
--
Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPS/TORAY SHENZHEN/A673M B
Shrinkage rate
TD:3.00mm2
内部方法
%
0
Shrinkage rate
MD:3.00mm4
内部方法
%
0
Water absorption rate
23°C,24hr
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPS/TORAY SHENZHEN/A673M B
shear strength
23°C
JISK7214
Mpa
6
Tensile strain
断裂,23°C
ISO527-2
%
2
Tensile stress
屈服,23°C
ISO527-2
Mpa
1
Taber abraser
1000Cycles
ISO9352
mg
5
Bending modulus
23°C
ISO178
Mpa
1
Bending stress
23°C
ISO178
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PPS/TORAY SHENZHEN/A673M B
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Melting temperature
ISO11357-3
°C
2
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
TD
ISO11359-2
cm/cm/°C
3
Electrical performance
Test Condition
Test Method
Unit
PPS/TORAY SHENZHEN/A673M B
Dielectric strength
IEC60243-1
KV/mm
2
Volume resistivity
IEC60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PPS/TORAY SHENZHEN/A673M B
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
6
Supplementary Information
Test Condition
Test Method
Unit
PPS/TORAY SHENZHEN/A673M B
BarFlowLength6
320°C,1.00mm
内部方法
mm
1