Melt volume flow rate

190°C/2.16kg

ISO1133

cm3/10min

1

Melt mass flow rate

ISO1133

g/10min

1

Shrinkage rate

TD

ISO294-4

%

1

Shrinkage rate

MD

ISO294-4

%

2

Water absorption rate

饱和,23°C,2.00mm

ISO62

%

0

Water absorption rate

平衡,23°C,2.00mm,50%RH

ISO62

%

0

Nominal tensile fracture strain

ISO527-2

%

2

Tensile modulus

ISO527-2

Mpa

3

Tensile strain

屈服

ISO527-2

%

1

Tensile stress

屈服

ISO527-2

Mpa

7

Bending modulus

ISO178

Mpa

3

Bending stress

3.5%应变

ISO178

Mpa

8

Hot deformation temperature

0.45MPa,未退火

ISO75-2/B

°C

1

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

1

Melting temperature 2

ISO11357-3

°C

1

Linear coefficient of thermal expansion

MD：--

ISO11359-2

cm/cm/°C

1

Linear coefficient of thermal expansion

MD：-40to23°C

ISO11359-2

cm/cm/°C

9

Linear coefficient of thermal expansion

TD：--

ISO11359-2

cm/cm/°C

1

Linear coefficient of thermal expansion

TD：-40to23°C

ISO11359-2

cm/cm/°C

9

Linear coefficient of thermal expansion

TD：AnnealingTemperature

ISO11359-2

°C

1

Linear coefficient of thermal expansion

TD：AnnealingTime-Optional

ISO11359-2

min/mm

3

Surface resistivity

IEC60093

ohms

>

Dielectric strength

IEC60243-1

KV/mm

4

Leakage Trace Index

IEC60112

V

6

Volume resistivity

IEC60093

ohms·cm

>

Impact strength of simply supported beam without notch

-30°C

ISO179/1eU

kJ/m²

2

Impact strength of simply supported beam without notch

23°C

ISO179/1eU

kJ/m²

2

Fogging-G-value

condensate

ISO6452

g

3

Burning rate 3

1.00mm

ISO3795

mm/min

<

Emission

VDA275

mg/kg

<

EmissionofOrganicCompounds

VDA277

µgC/g

1