Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPA/F/PTFE UFL-36S BK1A956 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electrical appliances、Electronic display、Car hood、bearing
Thermal stability、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPA/F/PTFE/SABIC INNOVATIVE US/UFL-36S BK1A956
Shrinkage rate (Across Flow)
xflow, 24
ASTM D 955
%
0
Shrinkage rate (Across Flow)
xflow, 24
ISO 294
%
0
Longitudinal shrinkage rate (Flow)
flow, 24 h
ISO 294
%
0
Longitudinal shrinkage rate (Flow)
flow, 24 h
ASTM D 955
%
0
Moisture absorption rate
50% RH,
ASTM D 570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPA/F/PTFE/SABIC INNOVATIVE US/UFL-36S BK1A956
Tensile strength fracture (brk)
/
ASTM D638
Mpa
1
Tensile strength fracture (brk)
/
ISO 527
Mpa
1
Tensile elongation fracture (brk)
/
ASTM D638
%
2
Tensile elongation fracture (brk)
/
ISO 527
%
2
friction coefficient
Dynamic
ASTM D 3702
/
0
friction coefficient
Static C
ASTM D 3702
/
0
Wear factor
Wear Fa
ASTM D 3702
in5·min/ft·lb·hr
6
Bending modulus
/
ASTM D790
Mpa
1
Bending modulus
/
ISO 178
Mpa
1
bending strength
/
ASTM D790
Mpa
2
bending strength
/
ISO 178
Mpa
2
Impact performance
Test Condition
Test Method
Unit
PPA/F/PTFE/SABIC INNOVATIVE US/UFL-36S BK1A956
Multi axis impact
/
ISO 6603
J
3
Izod Notched on Cantilever Beam
23℃ (73℉)
ISO 180/1A
kJ/m²
1
Cantilever beam without notch (Izod Unnotched)
23℃ (73℉)80*10*4
ISO 180/1U
kJ/m²
7
Instrumented dart impact energy peak at 23 ℃ (73 ℉)
/
ASTM D3763
J
7