PA6 BM73G15 THS BK317 DUPONT USA
Zytel®
Industrial machinery、Automotive components
Thermal stability、High crystallinity、Filler: Glass fiber reinf、15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA6/DUPONT USA/BM73G15 THS BK317
MeltViscosity
280°C,1000sec^-1
ISO11443
mPa·s
3
Shrinkage rate
TD
ISO294-4
%
1
Shrinkage rate
MD
ISO294-4
%
0
Water absorption rate
饱和,23°C,2.00mm
ISO62
%
7
Water absorption rate
平衡,23°C,2.00mm,50%RH
ISO62
%
2
Mechanical performance
Test Condition
Test Method
Unit
PA6/DUPONT USA/BM73G15 THS BK317
Tensile modulus
ISO527-2
Mpa
5
Tensile strain
断裂
ISO527-2
%
5
Tensile stress
断裂
ISO527-2
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PA6/DUPONT USA/BM73G15 THS BK317
Glass transition temperature 4
ISO11357-2
°C
6
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Melting temperature 5
ISO11357-3
°C
2
Electrical performance
Test Condition
Test Method
Unit
PA6/DUPONT USA/BM73G15 THS BK317
Leakage Trace Index
IEC60112
V
6
Volume resistivity
IEC60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PA6/DUPONT USA/BM73G15 THS BK317
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
8
flammability
Test Condition
Test Method
Unit
PA6/DUPONT USA/BM73G15 THS BK317
Extreme Oxygen Index
ISO4589-2
%
2
Burning rate 5
1.00mm
ISO3795
mm/min
<