PC/PBT VX5022-7001 SABIC INNOVATIVE US
XENOY™
Electronic and electrical、engineering application 、Automotive components
High mobility、High crystallinity、Aging resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/VX5022-7001
Melt flow rate
250°C/2.16 kg
ASTM D1238
g/10 min
1
Melt flow rate
265°C/5.0 kg
ASTM D1238
g/10 min
5
Melt flow rate
266°C/5.0 kg
ASTM D1238
g/10 min
5
Molten Volume Flow Rate (MVR)
250°C/2.16 kg
ISO 1133
cm3/10min
1
Molten Volume Flow Rate (MVR)
250°C/5.0 kg
ISO 1133
cm3/10min
2
Molten Volume Flow Rate (MVR)
265°C/5.0 kg
ISO 1133
cm3/10min
4
Shrinkage rate
流动 2
内部方法
%
0
Shrinkage rate
流动 : 3.20 mm
内部方法
%
0
Shrinkage rate
横向流动 2
内部方法
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/VX5022-7001
Tensile strength
屈服 4
ASTM D638
Mpa
1
Tensile strength
屈服
ISO 527-2/5
Mpa
1
Tensile strength
断裂 4
ASTM D638
Mpa
1
Tensile strength
断裂
ISO 527-2/5
Mpa
1
Tensile modulus
-- 3
ASTM D638
Mpa
7
Tensile modulus
--
ISO 527-2/1
Mpa
7
elongation
屈服 4
ASTM D638
%
3
elongation
屈服
ISO 527-2/5
%
3
elongation
断裂 4
ASTM D638
%
3
elongation
断裂
ISO 527-2/5
%
3
Bending modulus
50.0 mm 跨距 5
ASTM D790
Mpa
5
Bending modulus
-- 6
ISO 178
Mpa
6
Bending strain - at Break 8
ISO 178
%
3
Bending stress
-- 6, 7
ISO 178
Mpa
1
Bending stress
屈服, 50.0 mm 跨距 5
ASTM D790
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/VX5022-7001
Vicat softening temperature
--
ASTM D152511, ISO 306/A5011
°C
2
Vicat softening temperature
--
ASTM D152512, ISO 306/B50, ISO 306/B120
°C
1
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ASTM E831
cm/cm/°C
4
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ISO 11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
流动 : 23 到 60°C
ISO 11359-2
cm/cm/°C
4
Linear coefficient of thermal expansion
流动 : 23 到 80°C
ISO 11359-2
cm/cm/°C
4
Linear coefficient of thermal expansion
流动 : 23 到 150°C
ISO 11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
横向 : -40 到 40°C
ASTM E831
cm/cm/°C
1
Linear coefficient of thermal expansion
横向 : -40°C
ISO 11359-2
cm/cm/°C
6
Linear coefficient of thermal expansion
横向 : 23 到 60°C
ISO 11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
横向 : 23 到 80°C
ISO 11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
横向 : 23 到 150°C
ISO 11359-2
cm/cm/°C
1
Thermal deformation temperature under load
0.45 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 10
ISO 75-2/Bf
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 10
ISO 75-2/Af
°C
1
Electrical performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/VX5022-7001
Surface resistivity
IEC 60093
ohms
>
Dielectric strength
0.800 mm, in Oil
ASTM D149
KV/mm
3
Dielectric strength
1.60 mm, in Oil
ASTM D149
KV/mm
2
Dielectric strength
3.20 mm, in Oil
ASTM D149
KV/mm
1
Dielectric strength
0.800 mm, 在油中
IEC 60243-1
KV/mm
3
Dielectric strength
1.60 mm, 在油中
IEC 60243-1
KV/mm
2
Dielectric strength
3.20 mm, 在油中
IEC 60243-1
KV/mm
1
Leakage Trace Index
--
IEC 60112
V
2
Leakage Trace Index
解决方案 B
IEC 60112
V
1
Volume resistivity
--
ASTM D257
ohms·cm
>
Volume resistivity
--
IEC 60093
ohms·cm
>
Filling analysis
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/VX5022-7001
Melt viscosity
260°C, 1500 sec^-1
ISO 11443
Pa·s
2
Filling material
ASTM D152512, ISO 306/B50, ISO 306/B120
%
2
Impact performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/VX5022-7001
Impact strength of simply supported beam without notch
-30°C 9
ISO 179/1eU
kJ/m²
4
Impact strength of simply supported beam without notch
-30°C
ISO 179/2U
kJ/m²
5
Impact strength of simply supported beam without notch
23°C 9
ISO 179/1eU
kJ/m²
4
Impact strength of simply supported beam without notch
23°C
ISO 179/2U
kJ/m²
5
Non notched cantilever beam impact
-30°C
ASTM D4812
J/m
6
Non notched cantilever beam impact
23°C
ASTM D4812
J/m
6
Non notched cantilever beam impact
-30°C 10
ISO 180/1U
kJ/m²
3
Non notched cantilever beam impact
23°C 10
ISO 180/1U
kJ/m²
4
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
6
hardness
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/VX5022-7001
Ball pressure hardness
H 358/30
ISO 2039-1
Mpa
2
flammability
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/VX5022-7001
Extreme Oxygen Index
ISO 4589-2
%
2
Burning wire flammability index
1.0 mm
IEC 60695-2-12
°C
7
Burning wire flammability index
2.0 mm
IEC 60695-2-12
°C
8