PC/ABS MC1300-100 SABIC INNOVATIVE US
CYCOLAC™
Automotive sector
High impact resistance、High mobility、Easy electroplating
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE US/MC1300-100
Melt flow rate
260°C/5.0 kg
ASTM D1238
g/10 min
1
Shrinkage rate
流动 : 3.20 mm
内部方法
%
0
Shrinkage rate
横向流动 : 3.20 mm
内部方法
%
0
Water absorption rate
24 hr
ASTM D570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE US/MC1300-100
Tensile strength 3
屈服
ASTM D638
Mpa
5
Tensile strength 3
断裂
ASTM D638
Mpa
4
Tensile modulus 2
ASTM D638
Mpa
2
Elongation rate 3
屈服
ASTM D638
%
8
Elongation rate 3
断裂
ASTM D638
%
1
Bending modulus
50.0 mm 跨距
ASTM D790
Mpa
2
bending strength
屈服, 50.0 mm 跨距
ASTM D790
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE US/MC1300-100
thermal conductivity
ASTM C177
W/m/K
0
Vicat softening temperature
ASTM D15255
°C
1
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ASTM E831
cm/cm/°C
7
Linear coefficient of thermal expansion
横向 : -40 到 40°C
ASTM E831
cm/cm/°C
9
Thermal deformation temperature under load
0.45 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
9
Impact performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE US/MC1300-100
Dart impact equipped with measuring instruments
-30°C, Total Energy
ASTM D3763
J
3
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
4