Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EN-1052W FWA096 LOTTE KOREA
INFINO®
automotive industry
Fatigue resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/LOTTE KOREA/EN-1052W FWA096
Melt flow rate
250°C/10.0 kg
ASTM D1238, ISO 1133
g/10 min
3
Shrinkage rate
流动 : 3.20 mm
ASTM D955
%
0
Shrinkage rate
横向流动 : 3.20 mm
ASTM D955
%
0
Shrinkage rate
横向流量 : 2.00 mm
ISO 294-4
%
0
Shrinkage rate
流量 : 2.00 mm
ISO 294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/LOTTE KOREA/EN-1052W FWA096
Tensile strength
屈服 2
ASTM D638
Mpa
5
Tensile strength
屈服
ISO 527-2/50
Mpa
5
Tensile strength
断裂 2
ASTM D638
Mpa
5
Tensile strength
断裂
ISO 527-2/50
Mpa
6
Tensile modulus
-- 2
ASTM D638
Mpa
2
Tensile modulus
--
ISO 527-2/50
Mpa
2
elongation
断裂 2
ASTM D638
%
1
elongation
断裂
ISO 527-2/50
%
1
Bending modulus
-- 3
ASTM D790
Mpa
2
Bending modulus
-- 4
ISO 178
Mpa
2
bending strength
-- 3
ASTM D790
Mpa
7
bending strength
-- 4
ISO 178
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
PC/LOTTE KOREA/EN-1052W FWA096
Vicat softening temperature
ISO 306/B50
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm
ISO 75-2/A
°C
1