Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO WCD931 BK1006 SABIC INNOVATIVE JAPAN
FLEX NORYL™
Automotive interior parts
High impact resistance、transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE JAPAN/WCD931 BK1006
Melt mass flow rate
250°C/10.0kg
ASTMD1238
g/10min
8
Mechanical performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE JAPAN/WCD931 BK1006
Tensile strength
断裂
CCP METHOD
Mpa
1
Tensile strength
断裂2
ASTMD638
Mpa
9
Tensile strength
Break,80°C3
CCP METHOD
Mpa
1
Tensile strain
断裂
ISO527-2/50
%
1
Tensile stress
断裂
ISO527-2/50
Mpa
9
elongation
断裂
CCP METHOD
%
3
elongation
断裂2
ASTMD638
%
1
elongation
Break,80°C3
CCP METHOD
%
2
Bending modulus 4
100mmSpan
ASTMD790
Mpa
1
Bending modulus 4
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE JAPAN/WCD931 BK1006
HeatDeformation5
100°C
CCP METHOD
%
1
Brittle temperature
ASTMD746
°C
<
Electrical performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE JAPAN/WCD931 BK1006
Electrical strength
2.00mm,inOil
IEC60243-1
KV/mm
2
Leakage Trace Index
IEC60112
V
6
Volume resistivity
ASTMD257
ohms·cm
2
flammability
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE JAPAN/WCD931 BK1006
Extreme Oxygen Index
ISO4589-2
%
2
Hot filament ignition temperature
3.0mm
IEC60695-2-13
°C
7
Burning wire flammability index
3.0mm
IEC60695-2-12
°C
7