PA6 BKV30H2.0 901510 LANXESS WUXI
--
--
30% glass fiber reinforce、Easy to flow、Thermal stability rating
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Mechanical performance
Test Condition
Test Method
Unit
PA6/LANXESS WUXI/BKV30H2.0 901510
Bending stress at 3.5% strain
2mm/min
ISO 178
Mpa
2
Charpy notch impact strength
-30℃
ISO 179-1eA
kJ/m²
Fracture elongation rate
5mm/min
ISO 527-1,-2
%
3
Tensile modulus
1mm/min
ISO 527-1,-2
Mpa
9
tensile strength
5mm/min
ISO 527-1,-2
Mpa
1
Bending modulus
2mm/min
ISO 178
Mpa
8
bending strength
2mm/min
ISO 178
Mpa
2
Strain under bending strength
2mm/min
ISO 178
%
4
Thermal performance
Test Condition
Test Method
Unit
PA6/LANXESS WUXI/BKV30H2.0 901510
Hot deformation temperature method Af
1.80MPa
ISO 75-1,-2
°C
2
Hot deformation temperature - method Cf
8.00MPa
ISO 75-1,-2
°C
1
Processing performance
Test Condition
Test Method
Unit
PA6/LANXESS WUXI/BKV30H2.0 901510
Mold temperature
ISO 294
°C
8
Melt Temperature
ISO 294
°C
2
Injection speed
ISO 294
mm/s
2
Other performance
Test Condition
Test Method
Unit
PA6/LANXESS WUXI/BKV30H2.0 901510
Glass fiber/glass beads/filler content
ISO 3451-1
%
3