Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC ML-3120ZHP TEIJIN JAPAN
PANLITE®
Electrical tools、Lighting fixtures
Thermal stability、transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/TEIJIN JAPAN/ML-3120ZHP
Dissolving fingers
300℃
ISO 1133
cm310min
8
Mechanical performance
Test Condition
Test Method
Unit
PC/TEIJIN JAPAN/ML-3120ZHP
Tensile strength at break
50mm/min
ISO 527-1
Mpa
6
elongation at break
50mm/min
ISO 527-1
%
1
Tensile modulus
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
6
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
6
Yield tensile strength
50mm/min
ISO 527-1,2
Mpa
6
Gap impact strength
Notched
ISO 179
kJ/m²
2
Bending modulus
2mm/min
ISO 178
Mpa
2
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
9
bending strength
2mm/min
ISO 178
Mpa
9
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
2
Tensile elongation at break (elongation at break)
ASTM D638/ISO 527
%
1
Thermal performance
Test Condition
Test Method
Unit
PC/TEIJIN JAPAN/ML-3120ZHP
Hot deformation temperature
1.80MPa
ISO 75-1,2
°C
1
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
1
Linear expansion coefficient
ASTM D696/ISO 11359
mm/mm.℃
0
optical performance
Test Condition
Test Method
Unit
PC/TEIJIN JAPAN/ML-3120ZHP
Dispersion degree
2.0mmt
In-house method
%
6
Light transmittance
1.5mmt
JIS K7136
%
5