Apparent density

ISO60

g/cm³

0

Shrinkage rate

TD:280°C,3.00mm2

ISO2577

%

1

Shrinkage rate

TD:120°C,2hr,3.00mm3

ISO294-4

%

0

Shrinkage rate

MD:280°C,3.00mm2

ISO2577

%

0

Shrinkage rate

MD:120°C,2hr,3.00mm3

ISO2577

%

0

Water absorption rate

饱和,23°C

ISO62

%

5

Water absorption rate

平衡,23°C,50%RH

ISO62

%

2

Tensile strength

断裂,23°C

ASTMD638

Mpa

1

Tensile modulus

23°C

ASTMD638

Mpa

1

Tensile modulus

23°C

ISO527-2/1

Mpa

1

Tensile strain

断裂,23°C

ISO527-2/5

%

3

Tensile stress

断裂,23°C

ISO527-2/5

Mpa

1

elongation

断裂,23°C

ASTMD638

%

3

Bending modulus

23°C

ASTMD790

Mpa

8

Bending modulus 4

23°C

ISO178/A

Mpa

8

bending strength

23°C

ASTMD790

Mpa

2

Bending stress 4

3.5%Strain

ISO178/A

Mpa

-

Bending stress 4

23°C

ISO178

Mpa

2

Hot deformation temperature

0.45MPa,未退火

ISO75-2/B

°C

2

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

2

Hot deformation temperature

8.0MPa,未退火

ISO75-2/C

°C

1

Melting temperature 5

ISO11357-3

°C

2

Vicat softening temperature

ISO306/B120

°C

>

Linear coefficient of thermal expansion

MD：23到55°C

ISO11359-2

cm/cm/°C

2

Linear coefficient of thermal expansion

TD：23to55°C

ISO11359-2

cm/cm/°C

1

Surface resistivity

IEC60093

ohms

1

Dielectric strength

23°C,1.00mm

IEC60243-1

KV/mm

4

Leakage Trace Index

解决方案A

IEC60112

V

6

Volume resistivity

23°C

IEC60093

ohms·cm

1

Impact strength of simply supported beam without notch

-30°C

ISO179/1eU

kJ/m²

7

Impact strength of simply supported beam without notch

23°C

ISO179/1eU

kJ/m²

9

Ball pressure hardness

ISO2039-1

Mpa

2

Extreme Oxygen Index 7

ISO4589-2

%

2

Burning wire flammability index

2.0mm

IEC60695-2-12

°C

6