Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 5000M TAIDA TAIWAN
TAITALAC®
Household goods、Video tape
High rigidity、High gloss、Impact resistance、High gloss 、hard、Impact resistance、High rigidity、Highlight、Moderate impact resistanc
RoHS
TDS
TDS_ISO
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ABS/TAIDA TAIWAN/5000M
Melt flow index
200℃/5.0Kg
ASTMD1238
g/10min
1
Melt flow index
220℃/10.0Kg
ASTMD1238
g/10min
2
Melt flow rate
200℃/5.0 kg
ASTM D1238
g/10 min
1
Melt flow rate
220℃/10.0 kg
ASTM D1238
g/10 min
2
Shrinkage rate
MD
ASTM D955
%
<
Shrinkage rate
MD
ASTMD995
%
<
Water absorption rate
(23°C,24hr)
ASTMD570
%
<
Water absorption rate
饱和
ASTM D570
%
<
Mechanical performance
Test Condition
Test Method
Unit
ABS/TAIDA TAIWAN/5000M
elongation at break
23°C
ASTMD638
%
3
Tensile strength
屈服, 23℃, 3.18 mm
ASTM D638
Mpa
4
Tensile strength
断裂, 23℃, 3.18 mm
ASTM D638
Mpa
3
tensile strength
23°C
ASTMD638
Mpa
4
elongation
断裂, 23℃, 3.18 mm
ASTM D638
%
3
Bending modulus
23℃
ASTM D790
Mpa
2
Bending modulus
23°C
ASTMD790
Mpa
2
bending strength
23°C
ASTMD790
Mpa
7
bending strength
屈服, 23℃
ASTM D790
Mpa
7
Impact strength of cantilever beam gap
23℃, 3.18 mm
ASTM D256
J/m
2
Impact strength of cantilever beam gap
23℃, 6.35 mm
ASTM D256
J/m
1
Impact strength of cantilever beam gap
23°C
ASTMD256
J/m
2
Thermal performance
Test Condition
Test Method
Unit
ABS/TAIDA TAIWAN/5000M
High voltage arc tracing rate
1.57 mm
UL 746
mm/min
0
Hot deformation temperature
1.8 MPa, 退火, 12.7 mm
ASTM D648
°C
8
Hot deformation temperature
1.80MPa未退火
ASTMD648
°C
8
Hot wire ignition
1.57 mm
UL 746
sec
1
Vicat softening temperature
ASTM D1525
°C
1
Vicat softening temperature
ASTM1525
°C
1
Electrical performance
Test Condition
Test Method
Unit
ABS/TAIDA TAIWAN/5000M
Insulation strength
ASTMD149
KV/mm
2
Volume resistance
ASTMD257
Ω.cm
1
hardness
Test Condition
Test Method
Unit
ABS/TAIDA TAIWAN/5000M
Rockwell hardness
ASTMD785
R
1