Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 5010N6 JAPAN POLYPLASTIC
DURANEX®
--
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/JAPAN POLYPLASTIC/5010N6
Molten Volume Flow Rate (MVR)
250°C/2.16 kg
ISO 1133
cm3/10min
2
Shrinkage rate
横向流量 : 2.00 mm
内部方法
%
1
Shrinkage rate
流量 : 2.00 mm
内部方法
%
1
Water absorption rate
饱和, 23°C
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/JAPAN POLYPLASTIC/5010N6
Tensile modulus
ISO 527-2/1
Mpa
2
Tensile strain
屈服
ISO 527-2/50
%
4
Tensile strain
断裂
ISO 527-2/50
%
5
Tensile stress
屈服
ISO 527-2/50
Mpa
5
Bending modulus 3
ISO 178
Mpa
2
Bending stress 3
ISO 178
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PBT/JAPAN POLYPLASTIC/5010N6
RTI
0.71 mm
UL 746
°C
1
RTI Elec
0.71 mm
UL 746
°C
1
RTI Imp
0.71 mm
UL 746
°C
1
Hot deformation temperature
0.45 MPa, 退火
ISO 75-2/B
°C
1
Hot deformation temperature
1.8 MPa, 退火
ISO 75-2/A
°C
7
Melting temperature
ISO 11357-3
°C
2
Linear coefficient of thermal expansion
流动 : -30 到 35°C
ISO 11359-2
cm/cm/°C
8
Linear coefficient of thermal expansion
流动 : -30 到 120°C
ISO 11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
流动 : 35 到 120°C
ISO 11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
横向 : -30 到 35°C
ISO 11359-2
cm/cm/°C
8
Linear coefficient of thermal expansion
横向 : -30 到 120°C
ISO 11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
横向 : 35 到 120°C
ISO 11359-2
cm/cm/°C
1
Electrical performance
Test Condition
Test Method
Unit
PBT/JAPAN POLYPLASTIC/5010N6
Surface resistivity
IEC 60093
ohms
1
Dielectric strength
1.00 mm
IEC 60243-1
KV/mm
2
Dielectric strength
2.00 mm
IEC 60243-1
KV/mm
1
Volume resistivity
IEC 60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PBT/JAPAN POLYPLASTIC/5010N6
Impact strength of simply supported beam without notch
23°C
ISO 179
kJ/m²
1