Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 90G55 BK ASAHI JAPAN
Leona™
Automotive External Parts
Weather resistance、Good appearance、High rigidity、Glass fiber reinforced、high strength
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/90G55 BK
Shrinkage rate
横向流量
内部方法
%
0
Shrinkage rate
流量
内部方法
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
-
Mechanical performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/90G55 BK
Tensile modulus
23°C
ISO 527-2
Mpa
1
Tensile stress
断裂, 23°C
ISO 527-2
Mpa
2
Tensile stress
--
ASTM D638
Mpa
2
elongation
断裂
ASTM D638
%
2
elongation
断裂, 23°C
ISO 527-2
%
2
Bending modulus
--
ASTM D790
Mpa
1
Bending modulus
23°C
ISO 178
Mpa
1
bending strength
--
ASTM D790
Mpa
3
bending strength
23°C
ISO 178
Mpa
3
Thermal performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/90G55 BK
Hot deformation temperature
0.45 MPa, 未退火
ISO 75-2/B
°C
2
Hot deformation temperature
1.8 MPa, 未退火
ASTM D648, ISO 75-2/A
°C
2
Linear coefficient of thermal expansion - flow
ASTM D696
cm/cm/°C
2
Electrical performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/90G55 BK
Surface resistivity
ASTM D257, IEC 60093
ohms
1
Dielectric strength
ASTM D149, IEC 60243-1
KV/mm
2
Leakage Trace Index
3.00 mm
IEC 60112
V
4
Impact performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/90G55 BK
Impact strength of simply supported beam without notch
ISO 179
kJ/m²
8