Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 RF-1004HS SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic and electrical、Automotive components
Thermal stability、High temperature resistan、high strength、Filler: Glass fiber reinf、20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE US/RF-1004HS
Shrinkage rate
MD：24小时
ASTMD955
%
0
Shrinkage rate
TD：24hr
ASTMD955
%
1
Shrinkage rate
TD:24小时
ISO294-4
%
1
Shrinkage rate
MD:24小时
ISO294-4
%
0
Water absorption rate
24hr,50%RH
ASTMD570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE US/RF-1004HS
Tensile strength
断裂
ASTMD638
Mpa
1
Tensile modulus
ISO527-2/1
Mpa
7
Tensile modulus 2
ASTMD638
Mpa
7
Tensile strain
断裂
ISO527-2
%
3
Tensile stress
断裂
ISO527-2
Mpa
1
Wear factor - Washer
ASTMD3702Modified
10^-10in^5-min/ft-lb-hr
8
elongation
断裂
ASTMD638
%
3
Bending modulus
ASTMD790
Mpa
5
Bending modulus
ISO178
Mpa
7
bending strength
ASTMD790
Mpa
2
Bending stress
ISO178
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE US/RF-1004HS
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
2
Hot deformation temperature 4
1.8MPa,未退火,64.0mm跨距
ISO75-2/Af
°C
2
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
3
Linear coefficient of thermal expansion
MD：-40到40°C
ISO11359-2
cm/cm/°C
3
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：-40到40°C
ISO11359-2
cm/cm/°C
7
Impact performance
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE US/RF-1004HS
UnnotchedIzodImpactStrength3
23°C
ISO180/1U
kJ/m²
5
Multi axis Instrumented Impact Energy
ISO6603-2
J
2
Suspended wall beam gap impact strength 3
23°C
ISO180/1A
kJ/m²
8
Dart impact equipped with measuring instruments
23°C,EnergyatPeakLoad
ASTMD3763
J
1