Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS MP-0670 Samsung Cheil South Korea
STAREX®
Electrical enclosure、Automotive Applications
High mobility、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ABS/Samsung Cheil South Korea/MP-0670
Melt mass flow rate
200°C/5.0kg
ISO1133
g/10min
2
Melt mass flow rate
200°C/5.0kg
ASTMD1238
g/10min
2
Shrinkage rate
MD:3.20mm
ISO2577
%
0
Shrinkage rate
TD:3.20mm
ISO2577
%
0
Shrinkage rate
TD：3.20mm
ASTMD955
%
0
Shrinkage rate
MD：3.20mm
ASTMD955
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Water absorption rate
平衡,23°C
ASTMD570
%
0
Mechanical performance
Test Condition
Test Method
Unit
ABS/Samsung Cheil South Korea/MP-0670
Tensile strength 2
断裂
ASTMD638
Mpa
3
Tensile strength 2
屈服
ASTMD638
Mpa
4
Tensile modulus
ISO527-2/50
Mpa
2
Tensile modulus 2
ASTMD638
Mpa
2
Tensile strain
断裂
ISO527-2/50
%
3
Tensile stress
屈服
ISO527-2/50
Mpa
5
Tensile stress
断裂
ISO527-2/50
Mpa
3
Elongation rate 2
断裂
ASTMD638
%
2
Bending modulus 3
ASTMD790
Mpa
2
Bending modulus 4
ISO178
Mpa
2
Bending strength 3
ASTMD790
Mpa
6
Bending stress 4
ISO178
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
ABS/Samsung Cheil South Korea/MP-0670
Hot deformation temperature
0.45MPa,Unannealed,4.00mm
ISO75-2/B
°C
9
Hot deformation temperature
0.45MPa,Annealed,4.00mm
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
8
Hot deformation temperature
1.8MPa,Unannealed,4.00mm
ISO75-2/A
°C
8
Hot deformation temperature
1.8MPa,Annealed,4.00mm
ISO75-2/A
°C
9
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Impact performance
Test Condition
Test Method
Unit
ABS/Samsung Cheil South Korea/MP-0670
CharpyNotchedImpactStrength5
23°C
ISO179/1eA
kJ/m²
2
Suspended wall beam gap impact strength 5
23°C
ISO180/1A
kJ/m²
2
Suspended wall beam gap impact strength 5
-30°C
ISO180/1A
kJ/m²
8