density

ISO1183

g/cm³

1

density

ASTMD792

g/cm³

1

Melt viscosity

240°C,1000sec^-1

ASTMD3835

Pa·s

2

Melt mass flow rate

230°C/3.8kg

ASTMD1238

g/10min

6

Melt mass flow rate

220°C/10.0kg

ISO1133

g/10min

2

Shrinkage rate

MD：3.20mm

内部方法

%

0

Tensile strength

屈服

ASTMD638

Mpa

4

Tensile modulus

ASTMD638

Mpa

2

Tensile modulus

ISO527-2/1

Mpa

2

Tensile strain

屈服

ISO527-2/5

%

2

Tensile strain

断裂

ISO527-2/5

%

1

Tensile stress

断裂

ISO527-2/5

Mpa

3

Tensile stress

屈服

ISO527-2/5

Mpa

4

elongation

断裂

ASTMD638

%

5

Bending modulus

ISO178

Mpa

2

Bending modulus

50.0mm跨距

ASTMD790

Mpa

2

bending strength

屈服,50.0mm跨距

ASTMD790

Mpa

9

bending strength

ISO178

Mpa

7

Hot deformation temperature

0.45MPa,未退火,3.20mm

ASTMD648

°C

8

Hot deformation temperature

1.8MPa,未退火,3.20mm

ASTMD648

°C

7

Hot deformation temperature

1.8MPa,Unannealed,64.0mmSpan

ISO75-2/Af

°C

8

Vicat softening temperature

ISO306/B50

°C

9

Linear coefficient of thermal expansion

MD：-40到40°C

ISO11359-2

cm/cm/°C

6

Linear coefficient of thermal expansion

TD：-40到40°C

ISO11359-2

cm/cm/°C

6

Impact strength of cantilever beam gap

-40°C

ASTMD256

J/m

8

Impact strength of cantilever beam gap

23°C

ASTMD256

J/m

2

Impact strength of cantilever beam gap

23°C

ISO180/1A

kJ/m²

2

Impact strength of cantilever beam gap

-40°C

ISO180/1A

kJ/m²

7

Impact strength of cantilever beam gap

-30°C

ISO180/1A

kJ/m²

8

Dart impact equipped with measuring instruments

23°C,TotalEnergy

ASTMD3763

J

3