Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC PC- 122（9） TAIWAN CHIMEI
WONDERLITE®
packing、container
transparent、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/TAIWAN CHIMEI/PC- 122（9）
Density/specific gravity
23°C
ISO1183
g/cm³
1
Density/specific gravity 2
ASTMD792
g/cm³
1
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
2
Melt mass flow rate
300°C/1.2kg
ASTMD1238
g/10min
2
Shrinkage rate
ISO294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/TAIWAN CHIMEI/PC- 122（9）
Tensile strength 3
屈服
ASTMD638
Mpa
6
Tensile strain
断裂
ISO527-2/50
%
1
Tensile stress
屈服
ISO527-2/50
Mpa
6
Tensile stress
断裂
ISO527-2/50
Mpa
7
Elongation rate 4
断裂
ASTMD638
%
1
Bending modulus
ISO178
Mpa
2
Bending modulus 4
ASTMD790
Mpa
2
Bending strength 4
ASTMD790
Mpa
8
Bending stress 5
ISO178
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/TAIWAN CHIMEI/PC- 122（9）
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Hot deformation temperature
1.8MPa,退火
ISO75-2/A
°C
1
Hot deformation temperature 6
0.45MPa,Annealed
ASTMD648
°C
1
Vicat softening temperature
ASTMD15257
°C
1
Vicat softening temperature
--
ISO306/A50
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
6
Impact performance
Test Condition
Test Method
Unit
PC/TAIWAN CHIMEI/PC- 122（9）
Charpy Notched Impact Strength
23°C
ISO179
kJ/m²
6
Impact strength of cantilever beam gap
23°C,3.20mm
ASTMD256
J/m
8
Impact strength of cantilever beam gap
23°C
ISO180/4A
kJ/m²
6