Melt flow rate

280°C/5.0 kg

ASTM D1238

g/10 min

3

Molten Volume Flow Rate (MVR)

280°C/5.0 kg

ISO 1133

cm3/10min

3

Shrinkage rate - flow

3.20 mm

内部方法

%

0

Water absorption rate

24 hr, 23°C

ISO 62

%

0

Water absorption rate

24 hr, 23°C 2

ISO 62

%

0

Tensile strength

断裂 4

ASTM D638

Mpa

1

Tensile strength

断裂

ISO 527-2/50

Mpa

1

Tensile modulus

-- 3

ASTM D638

Mpa

7

Tensile modulus

--

ISO 527-2/1

Mpa

6

elongation

断裂 4

ASTM D638

%

3

elongation

断裂

ISO 527-2/50

%

2

Bending modulus

50.0 mm 跨距 5

ASTM D790

Mpa

5

Bending modulus

-- 6

ISO 178

Mpa

5

Bending stress

-- 6, 7

ISO 178

Mpa

1

Bending stress

屈服, 50.0 mm 跨距 5

ASTM D790

Mpa

1

Vicat softening temperature

--

ASTM D15259, ISO 306/B509

°C

1

Vicat softening temperature

--

ISO 306/B120

°C

1

Linear coefficient of thermal expansion

流动 : -40 到 40°C

ASTM E831

cm/cm/°C

2

Linear coefficient of thermal expansion

流动 : -40 到 40°C

ISO 11359-2

cm/cm/°C

3

Linear coefficient of thermal expansion

横向 : -40 到 40°C

ASTM E831

cm/cm/°C

7

Linear coefficient of thermal expansion

横向 : -40°C

ISO 11359-2

cm/cm/°C

7

Thermal deformation temperature under load

0.45 MPa, 未退火, 3.20 mm

ASTM D648

°C

1

Thermal deformation temperature under load

1.8 MPa, 未退火, 3.20 mm

ASTM D648

°C

1

Thermal deformation temperature under load

1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8

ISO 75-2/Af

°C

1

Surface resistivity

ASTM D257, IEC 60093

ohms

1

Dielectric strength

1.60 mm, in Oil

ASTM D149

KV/mm

2

Dielectric strength

1.50 mm, 在油中

IEC 60243-1

KV/mm

2

Volume resistivity

ASTM D257, IEC 60093

ohms·cm

2

Non notched cantilever beam impact

23°C

ASTM D4812

J/m

5

Non notched cantilever beam impact

-30°C 8

ISO 180/1U

kJ/m²

2

Non notched cantilever beam impact

23°C 8

ISO 180/1U

kJ/m²

2

Dart impact equipped with measuring instruments

23°C, Total Energy

ASTM D3763

J

1