Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 73M30 NC010 DUPONT USA
Zytel®
Electrical field、Electronic field、Automotive sector
Thermal stability、Easy electroplating
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PA6/DUPONT USA/73M30 NC010
Molding shrinkage rate
ASTM D955
%
0
physical property
Test Condition
Test Method
Unit
PA6/DUPONT USA/73M30 NC010
Shrinkage rate
TD
ISO294-4
%
0
Shrinkage rate
MD
ISO294-4
%
0
Water absorption rate
饱和,23°C,2.00mm
ISO62
%
6
Water absorption rate
平衡,23°C,2.00mm,50%RH
ISO62
%
2
Mechanical performance
Test Condition
Test Method
Unit
PA6/DUPONT USA/73M30 NC010
Tensile modulus
ISO527-2
Mpa
4
Tensile modulus
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
4
Tensile strain
断裂
ISO527-2
%
1
Tensile stress
断裂
ISO527-2
Mpa
8
Bending modulus
ISO178
Mpa
4
Thermal performance
Test Condition
Test Method
Unit
PA6/DUPONT USA/73M30 NC010
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
8
Melting temperature 2
ISO11357-3
°C
2
Vicat softening temperature
ISO306/B50
°C
2
Linear coefficient of thermal expansion
MD：--
ISO11359-2
cm/cm/°C
6
Linear coefficient of thermal expansion
MD：-40to23°C
ISO11359-2
cm/cm/°C
5
Linear coefficient of thermal expansion
MD：55to160°C
ISO11359-2
cm/cm/°C
8
Linear coefficient of thermal expansion
TD：--
ISO11359-2
cm/cm/°C
6
Linear coefficient of thermal expansion
TD：-40to23°C
ISO11359-2
cm/cm/°C
5
Linear coefficient of thermal expansion
TD：55to160°C
ISO11359-2
cm/cm/°C
1
Impact performance
Test Condition
Test Method
Unit
PA6/DUPONT USA/73M30 NC010
Impact strength of simply supported beam without notch
-30°C
ISO179/1eU
kJ/m²
8
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
1