Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL9300 SABIC INNOVATIVE US
LEXAN™
Electronic and Electrical、Aerospace Applications、lens
High mobility、Ductility at low temperat、Short molding cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/EXL9300
Density/specific gravity
ASTMD792
g/cm³
1
Density/specific gravity
ISO1183
g/cm³
1
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
7
Melt mass flow rate
300°C/1.2kg
ASTMD1238
g/10min
8
Shrinkage rate
MD：3.20mm
内部方法
%
0
Shrinkage rate
TD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/EXL9300
Tensile strength 3
屈服
ASTMD638
Mpa
5
Tensile strength 3
断裂
ASTMD638
Mpa
5
Tensile modulus
ISO527-2/1
Mpa
2
Tensile modulus 2
ASTMD638
Mpa
2
Tensile strain
断裂
ISO527-2/50
%
1
Tensile strain
屈服
ISO527-2/50
%
6
Tensile stress
断裂
ISO527-2/50
Mpa
5
Tensile stress
屈服
ISO527-2/50
Mpa
5
Elongation rate 3
屈服
ASTMD638
%
6
Elongation rate 4
断裂
ASTMD638
%
1
Bending modulus 4
50.0mm跨距
ASTMD790
Mpa
2
Bending modulus 5
ISO178
Mpa
2
Bending strength 4
屈服,50.0mm跨距
ASTMD790
Mpa
8
Bending strength 5,6
ISO178
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/EXL9300
RTIElec
UL746
°C
1
Evolution Calendar intelligent importer
UL746
°C
1
RTIStr
UL746
°C
1
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature 10
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
1
Hot deformation temperature 9
0.45MPa,Unannealed,100mmSpan
ISO75-2/Be
°C
1
Vicat softening temperature
ASTMD152511
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Vicat softening temperature
ASTMD152511
°C
1
Electrical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/EXL9300
Leakage Trace Index
IEC60112
V
2
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/EXL9300
Impact strength of simply supported beam gap 7
-30°C
ISO179/1eA
kJ/m²
5
Impact strength of simply supported beam gap 7
23°C
ISO179/1eA
kJ/m²
7
Suspended wall beam gap impact strength 8
23°C
ISO180/1A
kJ/m²
7
Suspended wall beam gap impact strength 8
-30°C
ISO180/1A
kJ/m²
5
flammability
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/EXL9300
GlowWireFlammability Index
1.9mm
IEC60695-2-12
°C
9
Hot filament ignition temperature
1.0mm
IEC60695-2-13
°C
9