Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6T C230N MITSUI CHEM JAPAN
ARLEN™
Electrical field、Electronic field
Glass fiber reinforced、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PA6T/MITSUI CHEM JAPAN/C230N
Molding shrinkage rate
ASTM D955
%
0
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
0
physical property
Test Condition
Test Method
Unit
PA6T/MITSUI CHEM JAPAN/C230N
Mold shrinkage rate
2mmt
ASTM D-955
%
0
Mechanical performance
Test Condition
Test Method
Unit
PA6T/MITSUI CHEM JAPAN/C230N
IZOD notch impact strength
dry(moist)
ASTM D-256
J/m
7
elongation at break
ASTM D638/ISO 527
%
4
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
1
tensile strength
dry(moist)
ASTM D-638
Mpa
1
tensile elongation
dry(moist)
ASTM D-638
%
3
Rockwell hardness
ASTM D-785
M Scale
1
Bending modulus
ASTM D638/ISO 527
%
1
Bending modulus
dry(moist)
ASTM D-790
Mpa
1
bending strength
dry(moist)
ASTM D-790
Mpa
2
bending strength
ASTM D790/ISO 178
%
2
Thermal performance
Test Condition
Test Method
Unit
PA6T/MITSUI CHEM JAPAN/C230N
Load deflection temperature
ASTM D-648
°C
2
Linear expansion coefficient
ASTM D696/ISO 11359
mm/mm.℃
3
Electrical performance
Test Condition
Test Method
Unit
PA6T/MITSUI CHEM JAPAN/C230N
Dielectric breakdown voltage
dry
ASTM D-149
KV/mm
2
Volume resistivity
dry
ASTM D-257
Ω.cm
1
Basic performance
Test Condition
Test Method
Unit
PA6T/MITSUI CHEM JAPAN/C230N
Water absorption rate
23℃,24小时在水里(2mmt,100℃)
ASTM D-570
%
0