Product Name
Brand Name
Usages
Properties
Certificates
PPA UC008H-BKNAT SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Mechanical parts、consumer goods
Thermal stability、Carbon fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPA/SABIC INNOVATIVE US/UC008H-BKNAT
Shrinkage rate
MD：24小时
ASTMD955
%
0
Shrinkage rate
TD：24hr
ASTMD955
%
0
Shrinkage rate
TD:24小时
ISO294-4
%
0
Shrinkage rate
MD:24小时
ISO294-4
%
0
Water absorption rate
24hr,50%RH
ASTMD570
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPA/SABIC INNOVATIVE US/UC008H-BKNAT
Tensile strength
断裂
ASTMD638
Mpa
2
Tensile modulus
ISO527-2/1
Mpa
3
Tensile modulus 2
ASTMD638
Mpa
3
Tensile strain
断裂
ISO527-2
%
1
Tensile stress
断裂
ISO527-2
Mpa
2
elongation
断裂
ASTMD638
%
1
Bending modulus
ASTMD790
Mpa
2
Bending modulus
ISO178
Mpa
2
bending strength
ASTMD790
Mpa
4
Bending stress
ISO178
Mpa
4
Thermal performance
Test Condition
Test Method
Unit
PPA/SABIC INNOVATIVE US/UC008H-BKNAT
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
>
Hot deformation temperature 4
1.8MPa,未退火,64.0mm跨距
ISO75-2/Af
°C
>
Electrical performance
Test Condition
Test Method
Unit
PPA/SABIC INNOVATIVE US/UC008H-BKNAT
Surface resistivity
ASTMD257
ohms
1
Volume resistivity
ASTMD257
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PPA/SABIC INNOVATIVE US/UC008H-BKNAT
UnnotchedIzodImpactStrength3
23°C
ISO180/1U
kJ/m²
4
Multi axis Instrumented Impact Energy
ISO6603-2
J
5
Suspended wall beam gap impact strength 3
23°C
ISO180/1A
kJ/m²
7
Dart impact equipped with measuring instruments
23°C,EnergyatPeakLoad
ASTMD3763
J
7