PPS OF-1006 SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic and electrical
Flame retardant、Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPS/SABIC INNOVATIVE US/OF-1006
Shrinkage rate
MD：24小时
ASTMD955
%
0
Shrinkage rate
TD：24hr
ASTMD955
%
0
Water absorption rate
24hr,50%RH
ASTMD570
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPS/SABIC INNOVATIVE US/OF-1006
Tensile strength 3
断裂
ASTMD638
Mpa
1
Tensile modulus
ISO527-2/1
Mpa
1
Tensile modulus 2
ASTMD638
Mpa
1
Tensile strain
断裂
ISO527-2/5
%
1
Tensile stress
断裂
ISO527-2/5
Mpa
1
Elongation rate 4
断裂
ASTMD638
%
1
Bending modulus 4
50.0mm跨距
ASTMD790
Mpa
1
Bending modulus 5
ISO178
Mpa
1
Bending strength 5
断裂,50.0mm跨距
ASTMD790
Mpa
1
Bending strength 5,6
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PPS/SABIC INNOVATIVE US/OF-1006
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
2
Hot deformation temperature 8
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
2
Hot deformation temperature 8
0.45MPa,Unannealed,64.0mmSpan
ISO75-2/Bf
°C
2
Linear coefficient of thermal expansion
MD：-30到30°C
ASTMD696
cm/cm/°C
2
Linear coefficient of thermal expansion
TD：-30to30°C
ASTMD696
cm/cm/°C
4
Impact performance
Test Condition
Test Method
Unit
PPS/SABIC INNOVATIVE US/OF-1006
NotchedIzodImpactStrength7
23°C
ISO180/1A
kJ/m²
5
UnnotchedIzodImpactStrength7
23°C
ISO180/1U
kJ/m²
2
Multi axis Instrumented Impact Energy
ISO6603-2
J
2