Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA/ABS N NM-11 BASF USA
Terblend®N
Helmet、Automotive sector、Application in the automo、sporting goods、Shell
High mobility、High impact resistance、Easy to process
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA/ABS/BASF USA/N NM-11
Melt volume flow rate
240°C/10.0kg
ISO1133
cm3/10min
3
Shrinkage rate
ISO294-4
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
1
Mechanical performance
Test Condition
Test Method
Unit
PA/ABS/BASF USA/N NM-11
Tensile modulus
ISO527-2
Mpa
2
Tensile strain
屈服,23°C
ISO527-2
%
3
Tensile stress
屈服,23°C
ISO527-2
Mpa
4
Bending modulus
ISO178
Mpa
1
Bending stress
ISO178
Mpa
6
Thermal performance
Test Condition
Test Method
Unit
PA/ABS/BASF USA/N NM-11
Hot deformation temperature 3
0.45MPa,退火
ISO75-2/B
°C
8
Hot deformation temperature 3
1.8MPa,退火
ISO75-2/A
°C
6
Vicat softening temperature
--
ISO306/A50
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
1
Electrical performance
Test Condition
Test Method
Unit
PA/ABS/BASF USA/N NM-11
Surface resistivity
IEC60093
ohms
1
Volume resistivity
IEC60093
ohms·cm
>
film
Test Condition
Test Method
Unit
PA/ABS/BASF USA/N NM-11
Elongation MD
断裂
ISO527-3
%
>
hardness
Test Condition
Test Method
Unit
PA/ABS/BASF USA/N NM-11
Ball pressure hardness
ISO2039-1
Mpa
8