Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS 1140A64 JAPAN POLYPLASTIC
DURAFIDE®
Electrical tools、Electrical field、Electronic field、Automotive sector、sporting goods、small home appliances
Glass fiber reinforced、High rigidity、high strength、High impact resistance、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1140A64
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
0
physical property
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1140A64
Water absorption rate
23°C,24hr
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1140A64
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
2
Tensile strain
断裂
ISO527-2
%
1
Tensile stress
ISO527-2
Mpa
2
Bending modulus
ISO178
Mpa
1
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
Bending stress
ISO178
Mpa
2
Tensile elongation at break (elongation at break)
ASTM D638/ISO 527
%
1
Thermal performance
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1140A64
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Linear expansion coefficient
ASTM D696/ISO 11359
mm/mm.℃
2
Electrical performance
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1140A64
Dissipation factor
耐电弧性
IEC60250
sec
1
Dielectric strength
3.00mm
IEC60243-1
KV/mm
1
Leakage Trace Index
IEC60112
V
1
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
4
Volume resistivity
IEC60093
ohms·cm
4
Filling analysis
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/1140A64
Melt viscosity
310°C,1000sec^-1
ISO11443
Pa·s
2