ABS PA-777E TAIWAN CHIMEI
POLYLAC®
Electrical field、Electronic field、Home appliance components、Automotive sector
Medium impact resistance、heat-resisting
MSDS
RoHS
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-777E
Density/specific gravity
--3
ASTMD792
g/cm³
1
Density/specific gravity
23°C
ISO1183
g/cm³
1
Melt volume flow rate
220°C/10.0kg
ISO1133
cm3/10min
4
Melt mass flow rate
220°C/10.0kg
ASTMD1238
g/10min
4
Shrinkage rate
ISO294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-777E
Tensile strength
屈服4
ASTMD638
Mpa
4
Tensile strength
屈服
ISO527-2/50
Mpa
4
Tensile strength
断裂
ISO527-2/50
Mpa
3
elongation
断裂4
ASTMD638
%
1
elongation
断裂
ISO527-2/50
%
2
Bending modulus
--5
ASTMD790
Mpa
2
Bending modulus
--6
ISO178
Mpa
2
bending strength
--5
ASTMD790
Mpa
6
bending strength
--6
ISO178
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-777E
Hot deformation temperature
1.8MPa,未退火
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Hot deformation temperature
1.8MPa,退火
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,退火
ISO75-2/A
°C
1
Vicat softening temperature
--
ASTMD15257,ISO306/A507
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
8
Impact performance
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-777E
Charpy Notched Impact Strength
-30°C
ISO179
kJ/m²
6
Charpy Notched Impact Strength
23°C
ISO179
kJ/m²
1
Impact strength of cantilever beam gap
23°C,3.20mm
ASTMD256
J/m
1
Impact strength of cantilever beam gap
23°C,6.40mm
ASTMD256
J/m
1
Impact strength of cantilever beam gap
-30°C
ISO180/1A
kJ/m²
6
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
1