elongation at break

ASTM D412/ISO 527

%

7

Tensile modulus

ASTM D412/ISO 527

kg/cm²(MPa)[Lb/in²]

2

Tensile modulus

MPa

2800

I

tensile strength

ASTM D638/ISO 527

kg/cm²(MPa)[Lb/in²]

8

Tensile strain

Yield

%

4.0

I

Tensile stress

Yield

MPa

80.0

I

Bending modulus

ASTM D790/ISO 178

kg/cm²(MPa)[Lb/in²]

3

Charpy notch impact strength

23°C

kJ/m²

3.0

I

Charpy impact strength

ASTM D256/ISO 179

kg·cm/cm(J/M)ft·lb/in

3

Charpy impact strength

ASTM D256/ISO 179

kg·cm/cm(J/M)ft·lb/in

不

IZOD notch impact strength

ASTM D256/ISO 179

kg·cm/cm(J/M)ft·lb/in

2

Hot deformation temperature

0.45 MPa

°C

115

I

Hot deformation temperature

1.8 MPa,未退火

°C

80.0

I

Hot deformation temperature

1.8 MPa

°C

80.0

I

Hot deformation temperature

0.45 MPa，未退火

°C

115

I

Melting temperature

°C

255

I

Linear coefficient of thermal expansion

Flow

cm/cm/°C

0.000070

I

Linear coefficient of thermal expansion

Transverse

cm/cm/°C

0.000070

I

density

kg/m³

1370

I

Shrinkage rate

Flow

%

1.8

I

Shrinkage rate

Across Flow

%

2.0

I

Water absorption rate

Saturation, 23°C

%

0.50

I

Water absorption rate

Saturation

%

0.50

I

Water absorption rate

Equilibrium, 23°C, 50% RH

%

0.20

I

Water absorption rate

Equilibrium

%

0.20

I