Melt volume flow rate

260°C/2.16kg

ISO1133

cm3/10min

1

260°C/2.16kg

ASTMD1238

g/10min

1

Shrinkage rate

MD：3.20mm

内部方法

%

0

Water absorption rate

饱和,23°C

ISO62

%

0

Water absorption rate

平衡,23°C,50%RH

ISO62

%

0

--

ASTMD638

Mpa

2

--

ISO527-2/1

Mpa

2

--

ISO178

Mpa

2

--

ISO178

Mpa

9

--

ISO178

Mpa

9

0°C

ASTMD256

J/m

4

0°C

ISO180/1A

kJ/m²

1

23°C

ISO180/1A

kJ/m²

2

23°C

ASTMD256

J/m

6

-30°C

ISO180/1A

kJ/m²

1

-30°C

ASTMD256

J/m

1

50.0mm span

ASTMD790

Mpa

2

Fracture

ASTMD638

%

1

crack

ISO527-2/50

%

9

Fracture

ASTMD638

Mpa

6

crack

ISO527-2/50

Mpa

4

Fracture, 50.0mm span

ASTMD790

Mpa

1

Surrender

ASTMD638

%

4

yield

ISO527-2/50

%

4

Surrender

ASTMD638

Mpa

6

yield

ISO527-2/50

Mpa

6

Yield, 50.0mm span of

ASTMD790

Mpa

1

Dart impact equipped with measuring instruments

23°C,TotalEnergy

ASTMD3763

J

6

--

ASTMD152518

°C

1

--

ISO306/B50

°C

1

--

ISO306/B120

°C

1

RTI

UL746

°C

8

RTIElec

UL746

°C

8

Evolution Calendar intelligent importer

UL746

°C

8

Hot deformation temperature

0.45MPa,未退火,3.20mm

ASTMD648

°C

1

Hot deformation temperature

1.8MPa,未退火,3.20mm

ASTMD648

°C

9

Linear coefficient of thermal expansion

MD:-40到40°C

ASTME831,ISO11359-2

cm/cm/°C

5

Linear coefficient of thermal expansion

TD:-40到40°C

ASTME831,ISO11359-2

cm/cm/°C

5

Surface resistivity

ASTMD257

ohms

>

Volume resistivity

ASTMD257

ohms·cm

>

Hot filament ignition temperature

1.00mm

IEC60695-2-13

°C

8

Hot filament ignition temperature

1.50mm

IEC60695-2-13

°C

8

Hot filament ignition temperature

3.00mm

IEC60695-2-13

°C

8

Burning wire flammability index

0.750mm

IEC60695-2-12

°C

9