Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 G-09S BLK01 MITSUBISHI ENGINEERING JAPAN
RENY™
Electronic and electrical、Automotive components
Low temperature resistanc、wear resistant、Filler: Glass fiber reinf、50% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/MITSUBISHI ENGINEERING JAPAN/G-09S BLK01
Melt volume flow rate
275°C/2.16kg
ISO1133
cm3/10min
2
Melt mass flow rate
275°C/2.16kg
ISO1133
g/10min
4
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PA66/MITSUBISHI ENGINEERING JAPAN/G-09S BLK01
Tensile modulus
ISO527-2
Mpa
1
Tensile strain
断裂
ISO527-2
%
1
Tensile stress
断裂
ISO527-2
Mpa
2
Bending modulus
ISO178
Mpa
1
Bending stress
ISO178
Mpa
3
Thermal performance
Test Condition
Test Method
Unit
PA66/MITSUBISHI ENGINEERING JAPAN/G-09S BLK01
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Impact performance
Test Condition
Test Method
Unit
PA66/MITSUBISHI ENGINEERING JAPAN/G-09S BLK01
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
6