Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPV 8201-90 CELANESE USA
Santoprene™
Kitchen utensils、Home appliance components、Fatigue relief supplies、Soft handle、Stationery、Smart phone、Kitchen utensils、Home appliance components、Fatigue relief supplies、Soft handle、Phone、Stationery
Low friction coefficient、Low mold expansion、Recyclable materials、Controllable mold expansi、Cleanable、Good melt strength、Good colorability、Ozone resistance、Chemical resistance、Low water absorption、Not absorbing water
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Thermal performance
Test Condition
Test Method
Unit
TPV/CELANESE USA/8201-90
RTIElec
UL746
°C
1
RTIStr
1.1mm
UL746
°C
9
RTIStr
1.6mm
UL746
°C
9
RTIStr
3.0mm
UL746
°C
9
Brittle temperature
ASTMD746
°C
-
Brittle temperature
ISO812
°C
-
ageing
Test Condition
Test Method
Unit
TPV/CELANESE USA/8201-90
ChangeinMassinAir
150°C,168hr
ASTMD573
%
-
ChangeinMassinAir
150°C,168hr
ISO188
%
-
Changes in tensile stress during fracture
23°C,168hr,inIRM903Oil
ISO1817
%
2
Changes in tensile stress during fracture
23°C,168hr,inSodiumChloride,15%
ISO1817
%
-
Changes in tensile stress during fracture
23°C,168hr,在水中
ISO1817
%
1
Changes in tensile stress during fracture
23°C,168hr,inSulfuricAcid,98%
ISO1817
%
6
Changes in tensile stress during fracture
23°C,168hr,inSodiumHydroxide,50%
ISO1817
%
0
Change rate of ultimate elongation
23°C,168hr,inIRM903Oil
ASTMD471
%
2
Change rate of ultimate elongation
23°C,168hr,inSodiumChloride,15%
ASTMD471
%
-
Change rate of ultimate elongation
23°C,168hr,inSodiumHydroxide,50%
ASTMD471
%
0
Change rate of ultimate elongation
23°C,168hr,inSulfuricAcid,98%
ASTMD471
%
6
Change rate of ultimate elongation
23°C,168hr,在水中
ASTMD471
%
1
Change rate of ultimate elongation in air
150°C,168hr
ASTMD573
%
-
Change rate of tensile strength in air
150°C,168hr
ASTMD573
%
1
Change rate of tensile strength in air
150°C,168hr
ISO188
%
1
Change rate of tensile strength
23°C,168hr,inIRM903Oil
ASTMD471
%
-
Change rate of tensile strength
23°C,168hr,inSodiumChloride,15%
ASTMD471
%
-
Change rate of tensile strength
23°C,168hr,inSodiumHydroxide,50%
ASTMD471
%
-
Change rate of tensile strength
23°C,168hr,inSulfuricAcid,98%
ASTMD471
%
4
Change rate of tensile strength
23°C,168hr,在水中
ASTMD471
%
1
Change rate of tensile strength
23°C,168hr,inIRM903Oil
ISO1817
%
-
Change rate of tensile strength
23°C,168hr,inSodiumChloride,15%
ISO1817
%
-
Change rate of tensile strength
23°C,168hr,inSodiumHydroxide,50%
ISO1817
%
-
Change rate of tensile strength
23°C,168hr,inSulfuricAcid,98%
ISO1817
%
4
Change rate of tensile strength
23°C,168hr,在水中
ISO1817
%
1
Quality change rate
23°C,168hr,inSulfuricAcid,98%
ASTMD471
%
1
Quality change rate
23°C,168hr,在水中
ASTMD471
%
-
Quality change rate
23.0°C,168hr,inWater
ISO1817
%
-
Quality change rate
23.0°C,168hr,inSulfuricAcid,98%
ISO1817
%
1
Quality change rate
23.0°C,168hr,inSodiumChloride,15%
ISO1817
%
1
Quality change rate
23.0°C,168hr,inSodiumHydroxide,50%
ISO1817
%
2
Quality change rate
23.0°C,168hr,inIRM903Oil
ISO1817
%
1
Quality change rate
23°C,168hr,inSodiumHydroxide,50%
ASTMD471
%
2
Quality change rate
23°C,168hr,inSodiumChloride,15%
ASTMD471
%
1
Quality change rate
23°C,168hr,inIRM903Oil
ASTMD471
%
1
elastomer
Test Condition
Test Method
Unit
TPV/CELANESE USA/8201-90
CompressionSet5
70°C,22hr
ISO815
%
5
TearStrength-AcrossFlow3
23°C
ISO34-1
kN/m
4
Tensile strength - transverse flow rate
断裂,23°C
ASTMD412
Mpa
1
Tensile strength TD
Break,23°C
ISO37
Mpa
1
Tensile stress transverse flow rate
100%应变,23°C
ASTMD412
Mpa
7
Tensile stress transverse flow rate
100%应变,23°C
ISO37
Mpa
7
Elongation rate - lateral flow rate
断裂,23°C
ASTMD412
%
6
Elongation rate - lateral flow rate
断裂,23°C
ISO37
%
6
Tear strength - transverse flow rate 2
23°C
ASTMD624
kN/m
4
Compression permanent deformation 4
70°C,22hr
ASTMD395B
%
5